牌号简介 About |
---|
Styrolux® 3G55是一种透明的苯乙烯-丁二烯共聚物(SBC),主要用于片材挤出和热成型应用。它是专门为提高与通用聚苯乙烯的混合性能而设计的,为零件提供了良好的韧性、透明度和经济性的平衡。由于堵塞的趋势,3G55主要用于直列式热成型。3G55含有微晶蜡,很难印刷和装饰。具有优异的韧性,高GPPS的混合能力,良好的透明度,应用于食品包装,食品服务,饮料杯,挤出薄膜,热成型。 Styrolux® 3G55 is a clear styrene butadiene copolymer (SBC) used mainly in sheet extrusion and thermoforming applications. It is specifically designed for improved performance in blends with general-purpose polystyrene, providing parts with an excellent balance of toughness, transparency and economics. Because of the tendency of blocking, 3G55 is mainly used in inline thermoforming. 3G55 is difficult to print and decorate since it contains a microcrystalline wax. FEATURES Outstanding toughness High GPPS blend capability Good transparency APPLICATIONS Food packaging Food service items Drinking cups Extruded films In-line thermoforming |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ASTM D792 |
密度 Density |
1.01 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
13 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
200℃,5 kg 200℃,5 kg |
14.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.30 to 1.0 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,23℃ Saturation, 23 ℃ |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
5% 应变 5% strain |
MPa | ||
-- -- |
MPa | ISO 178 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弹性模量 Elastic modulus |
|||
TD TD |
MPa | ASTM D882 | |
MD MD |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ISO 527-3 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD TD |
g | ASTM D1922 | |
氧气传输速率 Oxygen transfer rate |
|||
23℃,0% RH 23℃,0% RH |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
23℃ 23℃ |
g/m²/24 hr | ASTM F1249 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
23℃ 23℃ |
ASTM D256 | ||
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
Peak force Peak force |
J | ASTM D3763 | |
Total energy Total energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
|||
550 nm 550 nm |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0% to 85% RH gradient |
3 4h/80°C |
4 标准 B (120°C/h), 压 力1 (10N) |
5 Sodium D Line |
【新闻资讯】查看全部
南京今年将关停61家化工企业 已有5家开始关停或搬迁
2017-08-28 8月23日,南京市统计局发布南京化工行业调查报告。根据国家提出的长江经济带绿色发展部署,南京化工业迎来转型发展关键时期。今年南京将关停化工企业61家,其中已有5家开始关停或搬迁。而从化工企业的分布看,全市200多家企业,有100多家分布在六合区。 有机化学原料贡献近半产值 根据国家工信局调查口径,截至2016年12月,南京化工行业企业总数236家,涉及28个行业小类。累计实现总产值2391.01亿元,利税563.2亿元,利润177.68亿元。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |