牌号简介 About |
---|
类型:聚酯基级挤出和注塑级特点:优异的机械性能、高耐磨性、耐磨性、短周期应用:电线电缆、管道、输送带、鞋、密封件、屏蔽包、工程零件等 TYPE: Polyester-based grade Extrusion and injection molding grade FEATURES: Excellent mechanical properties, high abrasion resistance, wear resistance, short cycle times Applications: Wire & Cable, tubes, conveyor belt, shoes, seals, screenpacks, engineering parts, etc |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.21 | g/cm³ | ASTM D792 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
断裂 fracture |
45.0 | MPa | ASTM D412 |
100% 应变 100% strain |
19.0 | MPa | ASTM D412 |
300% 应变 300% strain |
37.0 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
380 | % | ASTM D412 |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395 | ||
23℃,24 hr 23℃,24 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
DIN Abrasion DIN Abrasion |
mm³ | ISO 4649 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
根据阻燃改性的特点制备聚丙烯泡沫
2019-03-01 聚丙烯(PP)是一种易燃材料,对聚丙烯进行阻燃改性尤为重要。近日,中科院宁波材料所郑文革研究员团队在制备高阻燃性能聚丙烯材料的基础上,采用超临界二氧化碳发泡技术协同单向牵伸法,制备出超轻、超强、高阻燃的聚丙烯泡沫。 该团队制备的聚丙烯泡沫结构独特,具有明显的各向异性。聚丙烯泡沫的密度仅为0.08g/cm3,但可支撑自重约30000倍的砝码,其比强度高达1813MPa/g・cm3,远超已知文献报道的聚合物泡沫。 不仅如此,这种聚丙烯泡沫因采用分散均匀的膨胀型阻 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |