牌号简介 About |
---|
VA-255是一种硬质聚氨酯,适用于手工批量和真空铸造法。无需使用汞、MOCA或TDI,室温固化即可获得优良的物理性能。VA-255具有优异的绿色强度,具有良好的拆卸特性。 VA-255 is a rigid polyurethane formulated for hand-batch and vacuum cast methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. VA-255 has excellent green strength for good demold characteristics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
Hardener Hardener |
1.11 | g/cm³ | |
固化处理 Curing treatment |
1.14 | g/cm³ | |
基体树脂 Matrix resin |
1.25 | g/cm³ | |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 到 0.60 | % | ASTM D2566 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
2760 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
粘度 viscosity |
|||
25℃ 25℃ 2 |
Pa·s | ||
25℃ 25℃ 3 |
Pa·s | ||
25℃ 25℃ 4 |
Pa·s | ||
固化时间 Curing time 5 |
hr | ||
胶凝时间 Gelation time |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
脱模时间 stripping time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Resin |
3 Mixed |
4 Hardener |
5 24 hours at 77°F + 4 hours at 150°F |
【新闻资讯】查看全部
南韩开发出使用葡萄糖制造塑料的技术
2018-02-01 南韩国际广播电台30日报导,南韩成功开发出了利用葡萄糖制造塑料的技术,研究结果刊登在国际学术杂志《自然通讯》(Nature Communications)上。 南韩科学技术信息通信部介绍,由南韩科学技术院(KAIST)生物化学工程系教授李相烨带领的研究组,和梨花女子大学化学新材料工程学院教授朴始宰教授(音)带领的研究组,成功开发出了这一塑料生产技术。 报导指出,研究组为了生产一种用于饮料瓶或食品包装材料的塑料「芳香族聚酯」,改变大肠杆菌的基因,然后为已变形的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |