牌号简介 About |
---|
Silopren® LSR 3285/50是一种双组分液体硅橡胶注射成型工艺。这种材料是制造需要自润滑特性的弹性体制品的最佳候选材料。自润滑效果是通过长时间从硫化胶中渗出的液体来实现的。通常在硫化后的几小时到一天之间开始。由Silopren® LSR 3285/50液态硅橡胶组成的硫化胶的主要特点和优点通常通过以下特性来区分:自润滑特性透明、低粘度、快速固化、高热稳定性、优异的耐老化性、易着色等潜在的应用,由于其优异的性能,Silopren® LSR 3285/50液体uid硅橡胶是一个很好的候选者考虑用于以下弹性体产品的线束应用:电缆密封套圈垫圈插头密封件 Silopren LSR 3285/50 is a two-component liquid silicone rubber for injection molding processes. This material is an excellent candidate to consider for the manufacture of elastomeric articles requiring self-lubricating properties. The self-lubricating effect is achieved by a fluid which exudes out of the vulcanizate over an extended period of time. It typically starts between a few hours and one day after vulcanization. Key Features and Benefits Vulcanizates consisting of Silopren LSR 3285/50 liquid silicone rubber are typically distinguished by the following properties: self-lubricating properties transparent low viscosity fast cure high thermal stability outstanding resistance to aging easy to color Potential Applications Because of the outstanding properties, Silopren LSR 3285/50 liquid silicone rubber is an excellent candidate to consider for use in wire harness applications for the following elastomeric articles: cable seals grommets gaskets plug seals |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | DIN 53479 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
53 | DIN 53505 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
10.9 | MPa | DIN 53504 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
530 | % | DIN 53504 |
撕裂强度 tear strength 2 |
40.0 | kN/m | ASTM D624 |
压缩形变 Compression deformation |
|||
175℃,22 hr 175℃,22 hr |
% | ISO 815 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
|||
< 27℃ < 27℃ |
wk | ||
后固化时间 Post curing time |
|||
200℃ 200℃ |
hr | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Vulcanization(175℃) Vulcanization(175℃) |
min | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 3 |
|||
-- -- 4 |
|||
粘度 viscosity |
DIN 53018 | ||
20℃ 20℃ 4 |
Pa·s | DIN 53018 | |
20℃ 20℃ 3 |
Pa·s | DIN 53018 | |
储存稳定性 storage stability |
|||
20 ℃ 20 ℃ |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Fluid Content Fluid Content |
|||
-- -- 3 |
% | ||
-- -- 4 |
% |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 模具 |
3 Part B |
4 Part A |
【新闻资讯】查看全部
巴斯夫:天然气限供有可能导致全球最大化工基地停产
2022-04-06 据德国报纸Frankfurter Allgemeine 报道,化工巨头巴斯夫发出警告,称如果俄罗斯的天然气供应中断,将造成严重后果。 巴斯夫表示,如果天然气供应减半,其欧洲业务将受到严重干扰。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |