| 牌号简介 About |
|---|
| Amodel AS- 4133 HS是33％玻纤增强、润滑、热稳定型聚邻苯二甲酰胺（PPA ），可快速加工、在水温模具中成型。常规应用包括电气和电子元件，尤其是汽车系统用电子电气元件。 - 黑色：AS-4133 HS BK 324 本色： AS-4133 HS NT Amodel® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO-1110, Accelerated Method. Typical applications include electrical and electronic components especially for automotive systems. Black: AS-4133 HS BK 324 Natural: AS-4133 HS NT |
产品描述 Product Description
用途：电气/电子应用领域;机器/机械部件;连接器;金属取代;阀门/阀门部件;手机;草坪和园林设备;厚壁配件（部件）;汽车领域的应用;工业应用;通用;工业部件;汽车电子;汽车的发动机罩下的零件;
颜色：自然色,黑色
加工条件：水温模具注塑成型
性能特点： 低吸湿性; 防火阻燃等级HB; 热稳定性好; 机械强度好; 激光加工-焊接; 尺寸稳定性好; 成型周期快; 耐化学性; 耐高温; 润滑性; 韧性好; Good Rigidity,Good flexibility,Good Dimensional Stability,Quick molding cycle,Laser welding,High Heat Resistance,Lubricating,Solvent resistance,Low moisture absorption,Heat Stabilized,HB
填料：玻璃纤维 33
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.45 | g/cm³ | ISO 1183/A |
|
收缩率 Shrinkage rate |
|||
|
TD TD |
1.0 | % | ASTM D955 |
|
MD MD |
0.50 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.29 | % | ASTM D570 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
11700 | MPa | ASTM D638 |
|
拉伸模量 Tensile modulus |
ISO 527-2 | ||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
100℃ 100℃ |
MPa | ISO 527-2 | |
|
150℃ 150℃ |
MPa | ISO 527-2 | |
|
175℃ 175℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
断裂，24℃ Fracture, 24 ℃ |
MPa | ISO 527-2 | |
|
断裂，150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
|
断裂，175℃ Fracture, 175 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
断裂 fracture |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
断裂，24℃ Fracture, 24 ℃ |
% | ISO 527-2 | |
|
断裂，150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
|
断裂，175℃ Fracture, 175 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
ISO 178 | ||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
100℃ 100℃ |
MPa | ISO 178 | |
|
150℃ 150℃ |
MPa | ISO 178 | |
|
175℃ 175℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
ISO 178 | ||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
100℃ 100℃ |
MPa | ISO 178 | |
|
150℃ 150℃ |
MPa | ISO 178 | |
|
175℃ 175℃ |
MPa | ISO 178 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
泊松比 Poisson's ratio |
ASTM E132 | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火，3.2 mm 1.8 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，退火，3.2 mm 0.45 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
|
连续使用温度 Continuous use temperature 2 |
℃ | ASTM D3045 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
熔融温度 Melting temperature |
℃ | ASTM D570 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
ASTM E831 | ||
|
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
|
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
|
MD MD |
ASTM E831 | ||
|
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
|
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
1.6 mm 1.6 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
mm/min | UL 746 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level 3 |
|||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Transmittance 4 |
ASTM D1003 | ||
|
1070 nm，1.60 mm 1070 nm，1.60 mm |
% | ASTM D1003 | |
|
1.60 mm，940 nm 1.60 mm，940 nm |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 1500小时 |
| 3 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
| 4 透光率，自然色牌号 |
|
【新闻资讯】查看全部 
凯米拉在北美完成乳液聚合物的产能扩张
2021-06-18 搜料网资讯： 6月17日，Kemira宣布已在其位于阿拉巴马州莫比尔的制造基地安装了新的最先进的 乳液 聚合物和生物基 丙烯酰胺 单体生产装置。生产已经开始，该设施预计将在 2021 年夏季 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付