| 牌号简介 About |
|---|
| ADIPRENE L 167聚氨酯橡胶是一系列液态聚氨酯聚合物之一，通过异氰酸酯基团与多胺或多元醇化合物的反应，可固化成强的、有弹性的固体。当用MBCA固化剂固化时，Adiprene L 167在95A硬度范围内生成硫化胶。其他固化体系可获得较低的硬度值和特殊性能。固化的阿迪普林L 167具有较高的拉伸强度和弹性，在低温下具有优异的性能。它能抵抗磨损、压缩变形、油、溶剂、氧化和臭氧。ADIPRENE L 167可以铸造或喷涂，以生产各种模制品和保护性和装饰性涂层。 ADIPRENE® L 167 urethane rubber is one of a series of liquid urethane polymers which can be cured to a strong, rubbery solid by reaction of the isocyanate groups with polyamine or polyol compounds. When cured with MBCA curing agent, ADIPRENE L 167 yields vulcanizates in the 95A durometer hardness range. Lower hardness values and special properties can be obtained with other curing systems. Cured ADIPRENE L 167 has high tensile strength and resilience and excellent properties at low temperatures. It is resistant to abrasion, compression set, oils, solvents, oxidation and ozone. ADIPRENE L 167 can be cast or sprayed to produce a variety of molded goods and protective and decorative coatings. |
产品描述 Product Description
用途：涂层应用;
加工条件：浇铸 casting
性能特点： 拉伸性能好; 耐磨; 耐油; 抗氧化; 耐化学性; 耐低温; 耐臭氧; 有弹性; Antifreeze,Inoxidizability,Elastic,Good Tensile Strength,Good wear resistance,Grease resistance,Ozone resistance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.14 | g/cm³ | ASTM D792 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
95 | ASTM D2240 | |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
100% 应变 100% strain |
12.4 | MPa | ASTM D412 |
|
300% 应变 300% strain |
23.4 | MPa | ASTM D412 |
|
拉伸强度 tensile strength |
34.5 | MPa | ASTM D412 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D412 | |
|
撕裂强度 tear strength |
|||
|
-- -- 2 |
kN/m | ASTM D624 | |
|
开裂 cracking |
kN/m | ASTM D470 | |
|
压缩形变 Compression deformation |
|||
|
70℃，22 hr 70℃，22 hr |
% | ASTM D395B | |
|
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
|
卡-伯模量 Kappa's modulus |
ASTM D1043 | ||
|
-57℃ -57℃ |
MPa | ASTM D1043 | |
|
-40℃ -40℃ |
MPa | ASTM D1043 | |
|
-18℃ -18℃ |
MPa | ASTM D1043 | |
|
24℃ 24℃ |
MPa | ASTM D1043 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient |
|||
|
NBS NBS |
|||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
固化时间 Curing time |
|||
|
100℃ 100℃ |
hr | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
ASTM D696 | ||
|
-36 到 0℃ -36 to 0 ℃ |
cm/cm/℃ | ASTM D696 | |
|
0 到 24℃ 0 to 24 ℃ |
cm/cm/℃ | ASTM D696 | |
|
24 到 100℃ 24 to 100 ℃ |
cm/cm/℃ | ASTM D696 | |
|
100 到 150℃ 100 to 150 ℃ |
cm/cm/℃ | ASTM D696 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
热固组件 Thermosetting components |
|||
|
树脂 resin |
|||
|
硬化法 Hardening method |
|||
|
储存稳定性 storage stability |
|||
|
85 ℃ 85 ℃ |
min | ||
|
脱模时间 stripping time |
|||
|
100℃ 100℃ |
min | ||
|
后固化时间 Post curing time |
|||
|
70℃ 70℃ |
hr | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具 |
|
【新闻资讯】查看全部 
14部门发文保障煤炭天然气运输
2022-01-15 搜料网资讯： 近日，国家发改委、交通运输部、公安部、人力资源社会保障部、应急部、市场监管总局等联合发布《关于全力做好2022年春运工作的意见》。 《意见》中明确，要强化货 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付