牌号简介 About |
---|
硅橡胶、LSR成型件、食品接触件、塑料和橡胶加工成型件、技术、塑料和橡胶加工成型件、汽车、塑料和橡胶加工成型密封件、塑料和橡胶加工减震器、汽车和运输 Silicone Rubber, LSR Molded Parts, Food Contact, Plastics and Rubber Processing Molded Parts, Technical, Plastics and Rubber Processing Molded Parts, Automotive, Plastics and Rubber Processing Molded Seals, Plastics and Rubber Processing Vibration Dampers, Automotive & Transportation |
技术参数 Technical Data | |||
---|---|---|---|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
Clear/Transparent | ||
密度 Density |
1.08 | g/cm³ | ISO 1183 |
粘度 viscosity |
180 | Pa·s | DIN 53019 |
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
20 | DIN 53505 | |
拉伸强度 tensile strength |
8.00 | MPa | DIN 53504 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | DIN 53504 | |
压缩形变 Compression deformation |
% | DIN ISO 815-B | |
撕裂强度 tear strength |
kN/m | ASTM D624-B | |
回弹性 Resilience |
% | DIN 53512 | |
耐电强度 Electrical strength |
kV/mm | DIN IEC 243 | |
体积电阻率 Volume resistivity |
ohms·cm | DIN IEC 93 | |
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
DIN VDE 0303 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
怎样处理塑料制品加工中的气泡成绩
2015-12-10 气泡常常发生在塑料制品最后接缝处或制品较厚的部分。制品在模型内首先是表面冷却,当外表面已冷却,中心部分仍处于热的状态。中心部分冷却时要收缩,而塑料表面已经冷却,因此只能由内部自己收缩而形成气泡。有许多厚的制件在出模时还没有气泡,但是经过数十秒钟后,在中心部分就有气泡出现。 气泡有几种情况,现象不同,原因也不同,分述如下: (1)较厚的制品,表面发胖而鼓 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |