牌号简介 About |
---|
SABIC LLDPE 218BE是一种带有添加剂包装的丁烯线性低密度聚乙烯树脂,通常设计用于更广泛的食品应用(不含TNPP)。良好的热稳定性允许在关键的挤压加工条件下使用树脂。SABIC LLDPE 218BE制备的薄膜与较低的MFR LLDPE树脂相比,具有更好的拉伸性能。应用吹塑膜:SABIC LLDPE 218BE通常用于食品应用(层压膜、阻挡膜),但也可用于工业包装,并作为与其他SABIC PE树脂在吹塑和铸膜应用中的混合伙伴。铸膜:SABIC LLDPE 218BE通常用于食品应用(层压膜、阻挡膜)和托盘手包。色母粒复合:适用于薄膜和吹塑应用中的添加剂色母粒(如滑模剂、防雾剂、防静电剂、热稳定剂)。本文所述产品尤其未经测试,因此未经验证可用于医药/医疗应用。 SABIC® LLDPE 218BE is a butene linear low density polyethylene resin with an additive package typically designed for a broader range of food applications (TNPP free). The good thermal stability allows to use the resin in critical extrusion processing conditions. Films produced from SABIC® LLDPE 218BE have better draw-down ability compared to lower MFR LLDPE resins. SABIC® LLDPE 218BE is a Linear Low Density Polyethylene natural resin typically used for wire and cable applications. SABIC® LLDPE 218BE contains a high level of antioxidants and does not contain any antiblock and/or slip agents. It also exhibits good Environmental Stress Crack Resistance (ESCR). Sufficient Cu-inhibitor should be added to meet specific ageing requirements. For jacketing applications, addition of Carbon Black or UV stabilizer is required. Application Blown Film: SABIC® LLDPE 218BE is typically used for food applications (lamination film, barrier film) but can also be used in industrial packaging and as blending partner with other SABIC® PE resins in both blown and cast film applications. Cast Film: SABIC® LLDPE 218BE is typically used for food applications (lamination film, barrier film) and pallet hand wrap. Masterbatch Compounding: It is suitable for additive masterbatches (eg. slip agents, anti fog agents, anti static agents, thermal stabilizers) in film and blow moulding applications. Wire & Cable Extrusion: Telecommunication and Power cable (LV, MV, HV) jacketing. Halogen-free flame retardant (HFFR) compounds. One-step or two-steps silane crosslinkable for cable insulation. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.1 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
Elastic Recovery(铸造薄膜,20.0 µm) Elastic Recovery (cast film, 20.0 µ m) |
53 | % | ASTM D5459 |
Protrusion Puncture Resistance - 铸造薄膜(20.0 µm) Corrosion Function Resistance - Cast thin film (20.0 µ m) |
2.20 | J | ASTM D5748 |
Retention Force(60 sec,20.0 µm) Retention Force(60 sec,20.0 µm) 2 |
g | ||
Stress Retention(铸造薄膜,20.0 µm) Stress Retention (cast film, 20.0 µ m) |
% | ASTM D5459 | |
Ultimate Pre(stretch Level 铸造薄膜,20.0 µm) Ultimate Pre-stretch Level - Cast Film (20.0 µm) |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 3 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ASTM D1003A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
J/cm | ISO 7765-2 | |
Peel Cling Peel Cling 2 |
ASTM D5458 | ||
0% pre-stretch:20.0 µm 0% pre-stretch:20.0 µm |
g/2.5 cm | ASTM D5458 | |
200% pre-stretch:20.0 µm 200% pre-stretch:20.0 µm |
g/2.5 cm | ASTM D5458 | |
撕裂强度 tear strength 2 |
|||
TD,20 µm TD,20 µm 2 |
kN/m | ISO 6383-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ASTM D638 | |
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
1% 正割 1% secant |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cast Film |
【新闻资讯】查看全部
欧盟塑料行业缺乏有效的可持续发展战略,6780亿欧元的投资者资本面临
2022-05-31 拐点已经到达了吗?根据Planet Tracker的一份新报告,这是投资者、监管机构和政界人士必须扪心自问的问题。事实上,新的打破常规报告假设,塑料行业的照常经营模式可能比开始向可持 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |