牌号简介 About |
---|
AClar33C是一种主要由三氟氯乙烯(CTFE)组成的共聚物膜。33c7.80 mil结合了优异的防潮性能、优异的耐化学性和机械强度。33C用于军事和工业包装应用。 Aclar 33C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). 33C 7.80 mil combines outstanding moisture barrier with excellent chemical resistance and mechanical strength. 33C is used for military and industrial packaging applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.12 | g/cm³ | ASTM D1505 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
MD:200 µm MD:200 µm |
1330 | MPa | ASTM D882 |
TD:200 µm TD:200 µm |
1330 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,200 µm MD, yield, 200 µ m |
27.0 | MPa | ASTM D882 |
TD,屈服,200 µm TD, yield, 200 µ m |
24.5 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服,200 µm MD, yield, 200 µ m |
% | ASTM D882 | |
TD,屈服,200 µm TD, yield, 200 µ m |
% | ASTM D882 | |
水气透过率 Water vapor transmittance |
|||
200 µm,38℃,100% RH 200 µm,38℃,100% RH |
g·mm/m²/atm/24 hr | ASTM F1249 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | ASTM D3418 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
|||
0.198 mm 0.198 mm |
% | ASTM D2863 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
198 µm 198 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
PC成为五大工程塑料中增长速度最快的通用工程塑料
2018-05-16 聚碳酸酯(PC)是一种综合性能优良的热塑性工程塑料,其电性能优良,吸水率低,透光性好,可见光的透过率可达90%以上,是五大通用工程塑料中唯一具有良好透明性的品种,同时又兼备较高的强度、延展性及韧性的品种,从而被广泛应用于电子电器、家电、建筑建材、汽车制造和医疗器械等领域。目前该材料已成为五大工程塑料中增长速度最快的通用工程塑料。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |