牌号简介 About |
---|
亚组均聚物描述窄分子量、低烟/冷凝应用建议用途包括细旦纺粘非织造布、高速纺-连续长丝纱。 Narrow MWD, low smoke / condensate Applications Suggested uses include fine denier spunbond nonwovens, high-speed spinning - continuous filament yarn |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
34 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
21 | J/m | ASTM D256-A |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Elongation of Fibers Elongation of Fibers 4 |
120 | % | ASTM D2256 |
Suggested Takeup Roll Speed Suggested Takeup Roll Speed |
66.7 | m/sec | Internal Method |
Tenacity of Fibers Tenacity of Fibers 4 |
2.30 | g/denier | ASTM D2256 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
1% 正割 1% secant 3 |
MPa | ASTM D790-A | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.050 in/min |
4 3.3 draw ratio, 1250 m/min roll speed, 225°C spin temp, D1000/68 |
【新闻资讯】查看全部
2017年独山子石化乙烯产量蝉联全国第一
2018-01-11 1月8日,记者从独山子石化公司规划计划处获悉,2017年生产乙烯132.15万吨,比上年增产1.35万吨,再创历史新高,蝉联全国第一。 2017年,独山子石化努力增产乙烯:一是让乙烯装置“吃饱”,外购乙烯原料85.3万吨,比上年提高9.2%;二是让乙烯装置“吃好”,推进裂解原料轻质化,轻质化比例达到25.86%;三是让乙烯装置“负重”,全年新区负荷率比上年提高1.55%;四是让乙烯装置“长跑”,开展劳动竞赛,激励员工精心操作、仔细巡检,保证了装置的长周期运行。 < |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |