| 牌号简介 About |
|---|
| 纤维素增强三聚氰胺模塑料非常好的电气性能，优异的表面硬度，良好的机械强度和耐热性，良好的磨损和紫外线稳定性，良好的滑动性能主要应用：电气工程中的模件，电弧室。本产品满足重金属和PCA，也符合欧盟指令2002/95（RoHS）、2002/96（WEEE）和2006/122（PFOS）的要求。 Cellulose reinforced Melamine moulding compound Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding behaviour Primary application(s): Moulded parts in electrical engineering, arc chambers This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
产品描述 Product Description
用途：电气元件;
加工条件：注射成型 Injection Molding
性能特点： 耐热性好; 防火阻燃等级V-0; 耐磨; 机械强度好; 硬度高; 电气性好; 耐候抗UV; Good Rigidity,Weather resistance is good,Good Electrical Properties,Good Hardness,Good wear resistance,Heat Resistance, Good,V-0
紫外线：UV Stabilized
填料：其他
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.50 到 1.70 | g/cm³ | ISO 1183 |
|
表观密度 Apparent density |
0.55 到 0.75 | g/cm³ | ISO 60 |
|
收缩率 Shrinkage rate 1 |
|||
|
MD MD 1 |
0.80 到 1.2 | % | ISO 2577 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
< 2.0 | % | ISO 62 |
|
后收缩 Post contraction 2 |
1.2 到 1.8 | % | ISO 2577 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
注塑成型 injection molding |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
注塑成型 injection molding |
MPa | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
压缩强度 compressive strength |
MPa | ISO 604 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：50~100℃ MD：50~100℃ |
1/℃ | ISO 11359-2 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
|
最高使用温度 Maximum operating temperature |
IEC 60216 | ||
|
<50 h <50 h |
℃ | ||
|
20，000 h 20，000 h |
℃ | ||
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
100 Hz 100 Hz |
|||
|
1 MHz 1 MHz |
|||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
|||
|
1 MHz 1 MHz |
|||
|
耐电弧性 Arc resistance |
ASTM D495 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.50 mm，Tested by RASCHIG 1.50 mm，Tested by RASCHIG |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
压缩成型压力 Compression molding pressure |
MPa | ||
|
压缩成型温度 Compression molding temperature |
℃ | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Injection Molded |
| 3 168 h / 110°C |
|
【新闻资讯】查看全部 
国家发改委：明年春耕用肥将得到进一步保障
2021-12-26 搜料网资讯： 12月16日上午，国家发改委举行新闻发布会，新闻发言人孟玮介绍了目前化肥生产的情况，并强调明年春耕农民用肥供应将得到进一步保障。 孟玮表示，今年以来，国内化 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付