BMC 620X模塑化合物是一种矿物填充,玻璃纤维增强聚酯化合物,适用于压缩,转移和填充注射成型。它是一种高冲击材料,以挤压形式生产,便于操作。其他特点是可塑性好,整体电气性能和阻燃性好。典型应用包括刷握、断路器外壳和焊枪手柄。BMC 620X模塑料是以各种工业颜色的挤压形式生产的。它有12英寸长的原木或特定重量的预切段塞,直径为1“至2½”。在这个范围内,较小的直径作为多个挤压件提供,重量公差为正负5%,最大为正负15克。 BMC 620X molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a high impact material produced in extruded form for ease of handling. Other characteristics are good moldability, excellent overall electrical properties and flame resistance. Typical applications include brush holders, circuit breaker housings and welding gun handles. BMC 620X molding compound is produced in extruded form in a range of industrial colors. It is available in logs up to 12 inches in length or as precut slugs, of specific weight, in diameters 1" to 2 ½" . Within this range, smaller diameters are supplied as multiple extrusions and weight tolerances are plus or minus 5 %, up to a maximum of plus or minus 15 grams. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.79 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:模压成型 MD: Compression molding |
0.25 到 0.35 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.19 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
320 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,模压成型 1.8 MPa, unannealed, molded |
260 | ℃ | ASTM D648 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 1 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.59 mm 1.59 mm |
|||
3.20 mm 3.20 mm |
|||
6.35 mm 6.35 mm |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
2018首个水性封闭剂树脂企业标准成功备案
2018-01-17 1月10日,全国企业标准公共信息平台正式发布 2018年备案的首个水性封闭剂树脂企业标准。这个由广东海顺新材料科技有限公司(以下简称:海顺科技)备案的企标,其核心产品――海顺木装甲以“耐冻融性(-15℃)不变质”的优秀性能,引发行业高度关注。 海顺木装甲-15℃不变质,可降低物流和仓储成本 企业生产的水性木器涂料是根据产品在5℃以上进行施工和贮存设计的。由于水性涂料对储存温度十分敏感,大部分水性涂料生产商建议温度要保持在0℃以上。 如果当地夜 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |