牌号简介 About |
---|
Titanvene™ LL0335AA是一种线性低密度聚乙烯,设计用于硅烷交联低压电力电缆绝缘、浇铸膜和旋转成型内层。Titanvene™ LL0335AA性能优良,凝胶含量低,易挤出。应用于硅橡胶工艺的低压电力电缆绝缘。铸膜。用于旋转成型(非紫外线)的内层推荐的加工条件Titanvene™ LL0335AA可以在正常机器上在150°C至220°C的温度范围内轻松加工。食品接触合规性Titanvene™ LL0335AA可用于食品接触应用。请联系最近的患者。Lotte Chemical Titan Nusantara代表详细了解特定等级的食品接触合规声明。 Titanvene™ LL0335AA Titanvene™ LL0335AA is a linear low density polyethylene designed for silane crosslinked low voltage power cable insulation, casting film and inner layer for rotomolding. Titanvene™ LL0335AA characterized by high speed performance, low gel content, easy extrusion. Applications Low voltage power cable insulation for sioplas process. Casting film. Inner layer for rotomolding (Non UV) Recommended Processing Conditions Titanvene™ LL0335AA can be easily processed on normal machines at temperatures in the range of 150°C to 220°C. Food Contact Compliance Titanvene™ LL0335AA can be used in food contact applications. Please contact your nearest PT. Lotte Chemical TITAN Nusantara representative for more detail of food contact compliance statements for the specific grade. Titanvene™ LL0335AA Titanvene™ LL0335AA is a linear low density polyethylene designed for silane crosslinked low voltage power cable insulation, casting film and inner layer for rotomolding. Titanvene™ LL0335AA characterized by high speed performance, low gel content and easy extrusion. Applications Low voltage power cable insulation for sioplas process. Casting film. Inner layer for rotomolding (Non UV) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate 2 |
|||
190℃,2.16kg 190℃,2.16kg 2 |
3.5 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient 4 |
0.80 | BS 2782 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 5 |
ISO 1184 | ||
屈服 yield 3 |
12.0 | MPa | ISO 527-2/2 |
MD,屈服 MD, yield |
11.0 | MPa | ISO 1184 |
TD,屈服 TD, yield |
MPa | ISO 1184 | |
拉伸应变 Tensile strain 5 |
ISO 1184 | ||
断裂 fracture 3 |
% | ISO 527-2/2 | |
MD,断裂 MD, fracture |
% | ISO 1184 | |
TD,断裂 TD, fracture |
% | ISO 1184 | |
落锤冲击 Drop hammer impact |
g | ISO 7765-1/A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature 6 |
|||
DSC DSC 6 |
℃ | ISO 3146 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
透明度 transparency |
ASTM D1746 | ||
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Condition 4 |
3 Molded Plaque, Speed C |
4 Method 824A |
5 Speed 1 |
6 Method C |
【新闻资讯】查看全部
十三届全国人大五次会议举行预备会议
2022-03-05 十三届全国人大五次会议4日上午在北京人民大会堂举行预备会议。全国人大常委会委员长栗战书主持会议。会议选举产生了十三届全国人大五次会议主席团和秘书长,表决通过了十三届 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |