牌号简介 About |
---|
TC-1604 A/B是一种填充的、易于应用的层压环氧树脂,适用于各种制造应用。设计用于较重的玻璃纤维布(通常为8-10 oz.工装织物),TC-1604可以生产厚层压板,而不会过度排出树脂。作为一个非常稳定的低收缩系统,其常用的用途包括:钻孔和修整夹具、模式/铸造应用、硅手套模具的复合工具支撑壳。对于不需要工作温度高于224°F(107°C)的应用,它具有在室温下固化的能力。TC-1604还可用作木材、复合材料和其他材料的粘合剂。添加填充剂,如气相二氧化硅,微球和短链纤维,可以创建填充剂,整流罩和粘合应用的糊状物。 TC-1604 A/B is a filled, easy to apply, laminating epoxy resin for variety of fabricating applications.Designed to be used with heavier weight fiberglass cloth (typically 8-10 oz. tooling fabric), TC-1604 can produce thick laminates without excess draining of the resin. Being a very stable system with low shrinkage, its common usages include: Drill and Trim Fixtures Pattern/Foundry Applications Composite Tooling Support Shells for Silicone Glove Molds. It features the ability to cure at room temperature for applications that do not require a working service temperature above 224°F (107°C). TC-1604 can also be used as an adhesive for bonding wood, composites, and other materials. Adding fillers like fumed silica, micro-spheres, and short-strand fibers can create pastes for fillets, fairings, and bonding applications. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
89 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
屈服 yield |
221 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
15900 | MPa | ASTM D790 |
弯曲强度 bending strength |
269 | MPa | ASTM D790 |
压缩强度 compressive strength |
276 | MPa | ASTM D695 |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
密度 Density |
|||
Part A:25℃ Part A:25℃ |
g/cm³ | ||
Part B:25℃ Part B:25℃ |
g/cm³ | ||
吸水率 Water absorption rate |
|||
100hr 100hr |
% | ASTM D570 | |
收缩率 Shrinkage rate |
% | ASTM D2566 | |
布络克菲尔德粘度 Brookfield viscosity |
|||
混合,25℃ Mixing, 25 ℃ |
Pa·s | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D3386 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
wk | ||
工作时间 working hours 2 |
|||
25℃ 25℃ 2 |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1 lb mass |
【新闻资讯】查看全部
环保组织估量到2050年英国陆地塑料垃圾将比鱼多
2017-07-18 据马来西亚《中国报》报道,环保组织“绿色和平”实地调查苏格兰30个沙滩后,发现每一个沙滩都被塑料制品污染,严重危害海鸟、鲨鱼、海豹和鲸鱼的生存环境。“绿色和平”估计,到2050年,英国99%本土海鸟都会吞下一定程度的塑料垃圾,届时海中的塑料垃圾将会比海鱼多,危及600种不同物种。 据悉,塑料表面会积聚藻类,散发出类似小磷虾的气味,因而吸引很多海鸟误吃。而塑料垃圾在海上漂浮时吸收了毒素,雀鸟误吞海洋垃圾等同服毒。此外,海洋垃圾也会令它们哽喉,损害它们的胃壁,甚至塞满它们的胃部 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |