牌号简介 About |
---|
VIPEL F085系列是一种溶于苯乙烯的环氧酚醛乙烯基酯树脂。085系列非常适用于需要优异的机械性能和耐化学、氧化和耐热性的应用。有利于耐腐蚀。环氧树脂-酚醛树脂主干化学提供了耐酸和碱的性能,并对许多有机溶剂具有优异的耐性。F085系列通常比标准双酚A环氧乙烯基酯树脂在更高温度下耐液体和蒸汽。F085系列产品非常适合氯碱电解领域使用。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀信息或有关树脂对任何特定化学环境的适用性问题,请联系AOC。机械性能F085系列适用于承受特别高静、动载荷的模具。它在高载荷下能抵抗内应力开裂。用途广泛,适用于各种加工方法,如手糊、缠绕等。 The Vipel F085 series is an epoxy novolac vinyl ester resin dissolved in styrene. 085 series is ideally suited for applications where outstanding mechanical properties and resistance to chemicals, oxidation and heat are required. BENEFITS Corrosion Resistance The epoxy novolac backbone chemistry provides resistance to acids and bases and has superior resistance to many organic solvents. The F085 series is generally resistant to liquids and vapors at higher temperatures than standard bisphenol-A epoxy vinyl ester resins. The F085 series is well suited for use in the field of chlorine-alkali electrolysis. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment, contact AOC. Mechanical Properties The F085 series is suitable for moldings that are subjected to particularly high static and dynamic loads. It is resistant to internal stress cracking under high loading. Versatile Suitable for various fabricating methods such as hand lay-up, filament winding, etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
35 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
149 | ℃ | ASTM D648 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
7.0 | min | |
放热峰值 exothermic peak |
216 | ℃ | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.07 | g/cm³ | |
粘度 viscosity |
|||
布络克菲尔德 RVT,25℃ 25℃,Brookfield RVT |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
国际油价迈向百元大关 国内油价或迎“四连涨”
2022-02-14 国内春节长假期间,国际油价在诸多利好下创出自2016年以来新高,过去的一周涨势不止,迈向百元大关。受此影响,2月17日24时,国内油价大概率上调,或迎来四连涨。 2月份以来,国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |