牌号简介 About |
---|
GM4755F是一种高分子量高密度聚乙烯。GM4755F用于生产厚度大于10微米的吹塑薄膜。典型应用包括手提包和衬里。应通过适当的性能测试来确定在任何应用中的适用性。GM4755F适用于食品接触应用,符合美国食品药品管理局CFR 21 177.1520第(c)段第3.1项的要求。 Alkatane GM4755F is a high molecular weight High Density Polyethylene grade with high toughness and stiffness. Film Extrusion: Alkatane GM4755F is designed for liners and carry bags where high impact, toughness and stiffness are required. It is also suitable for heavy duty films, where it may be blended with LLDPE or LDPE to enhance stiffness and yield strength while retaining toughness. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.949 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.10 | g/10min | ASTM D1238 |
190℃,5.0kg 190℃,5.0kg |
0.30 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
1100 | MPa | ASTM D790 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
15 | µm | |
拉伸强度 tensile strength |
|||
MD,屈服,15 µm MD, yield, 15 µ m |
MPa | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
15 µm 15 µm |
g | ASTM D1709 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫推出碳纤维增强型PPA用于替代铝和镁
2021-07-30 搜料网资讯: 巴斯夫现在提供碳纤维增强型聚邻苯二甲酰胺(PPA),填充率为20%、30%和40%。这些新材料的好处是,它们可以制造出重量极轻的部件,可以安全地取代铝和镁而不损失刚度 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |