P-70是一种高硬度、铂催化的RTV-2硅橡胶。它很容易混合和脱气,并将治愈几乎没有收缩。橡胶硬化的速度可以通过加热或室温下的铂加速器显著加快。在250°F下固化两小时后,硬度将增加到70。加成固化的双组分硅橡胶具有抑制敏感性。P-70具有优异的耐化学性和耐热性,以及抵抗大多数聚氨酯泡沫膨胀的刚性。 P-70 is a high durometer, platinum-catalyzed, RTV-2 silicone rubber. It is easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. A two hour post-cure at 250°F will increase the hardness to 70. Addition-cure two-component silicone rubbers may show inhibition sensitivity. P-70 offers outstanding chemical and heat resistance and the rigidity to withstand the expansion of most polyurethane foams. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 3 |
Green | ||
-- -- 4 |
Tan | ||
粘度 viscosity |
|||
-- -- 3 |
1.0 到 2.0 | Pa·s | |
-- -- 4 |
140 到 160 | Pa·s | |
固化时间 Curing time |
hr | ||
储存稳定性 storage stability |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A 5 |
|||
邵氏 A Shaw's A 6 |
|||
邵氏 A Shaw's A 7 |
|||
拉伸强度 tensile strength |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
耐电强度 Electrical strength |
kV/mm | ||
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
|||
体积电阻率 Volume resistivity |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
|||
Coverage(Cured) Coverage(Cured) |
cm³/g | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
使用温度 Operating temperature |
|||
Cured Cured |
℃ | ||
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
贮藏期限 Storage period |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Mixed |
3 Activator |
4 Base |
5 1 Day |
6 7 Days |
7 Post-Cured |
【新闻资讯】查看全部
VivoBarefoot推出一款新型生物基资料鞋
2018-09-25 VivoBarefoot公司计划于2019年推出一款新型生物基材料鞋系列产品。Primus Bio系列将在鞋底和鞋面使用玉米基TPU。 该公司表示,60%的外底和30%的鞋面是由生物基TPU制成,这种生物 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |