| 牌号简介 About |
|---|
| Bayflex MP-5000是一种固体弹性体，室温下的弯曲模量为5000 psi（35 MPa）。*在反应注射成型（RIM）设备上加工，用于辊、垫圈和密封窗口。该系统结合了快速拆卸时间、良好的拆卸完整性、改进的释放特性和出色的物理性能。与任何产品一样，在给定应用中使用Bayflex MP-5000系统必须由用户提前进行测试（包括现场测试等），以确定其适用性。Bayflex MP-5000是作为两种液体成分提供的配方RIM系统。A组分为二苯基甲烷二异氰酸酯（MDI）预聚物，B组分为聚醚多元醇。注意：在将内容物从桶转移到日计量箱之前，应彻底搅动部件B。 Bayflex MP-5,000 is a solid elastomer which has a flexural modulus of 5,000 psi (35 MPa) at room temperature.* It is processed on reaction injection molding (RIM) equipment and is used for rollers, gaskets, and encapsulated windows. This system combines rapid demold times, excellent integrity at demold, improved release characteristics and outstanding physical properties. As with any product, use of the Bayflex MP-5,000 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. Bayflex MP-5,000 is a formulated RIM system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol. Note: Component B should be agitated thoroughly prior to transfer of contents from the drum to the day tank. |
产品描述 Product Description
用途：门窗;滚轴;垫圈;
加工条件：反应注射成型 (RIM)
性能特点： 含脱模剂; Good stripping performance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
|||
|
-- -- |
0.998 | g/cm³ | ASTM D792 |
|
-- -- |
1.00 | g/cm³ | ASTM D1622 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.0 mm MD：3.0 mm |
1.3 | % | 内部方法 |
|
吸水率 Water absorption rate |
|||
|
10days，3.00 mm 10days，3.00 mm |
5.0 | % | 内部方法 |
|
24hr，3.00 mm 24hr，3.00 mm |
3.3 | % | 内部方法 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
断裂，3 mm Fracture, 3 mm |
MPa | ASTM D412 | |
|
断裂，3 mm Fracture, 3 mm |
MPa | ASTM D638 | |
|
20% 应变 20% strain 2 |
MPa | ASTM D412 | |
|
50% 应变，3 mm 50% strain, 3 mm 3 |
MPa | ASTM D412 | |
|
100% 应变，3 mm 100% strain, 3 mm 3 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，3 mm Fracture, 3 mm |
% | ASTM D412 | |
|
撕裂强度 tear strength 4 |
|||
|
3.00 mm 3.00 mm 4 |
kN/m | ASTM D624 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Water Immersion（Length Increase，3.00 mm） Water Immersion（Length Increase，3.00 mm） |
% | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，3.00 mm Shore A, 3.00 mm |
ASTM D2240 | ||
|
邵氏 D，3.00 mm Shore D, 3.00 mm |
ASTM D2240 | ||
|
弯曲模量 Bending modulus |
ASTM D790 | ||
|
-30℃，3 mm -30℃，3 mm |
MPa | ASTM D790 | |
|
23℃，3 mm 23℃，3 mm |
MPa | ASTM D790 | |
|
65℃，3 mm 65℃，3 mm |
MPa | ASTM D790 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：3 mm MD：3 mm |
1/℃ | ASTM D696 | |
|
低温脆性 Low temperature brittleness |
|||
|
-50℃，3.00 mm -50℃，3.00 mm |
ASTM D746 | ||
|
热固组件 Thermosetting components 5 |
|||
|
部件 A Component A |
|||
|
部件 B Component B |
|||
|
贮藏期限 Storage period |
|||
|
30℃ 30℃ |
wk | ||
|
脱模时间 stripping time |
min | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Die C, 20 in/min |
| 3 C 模具, 20 in/min |
| 4 C 模具 |
| 5 105 Index |
|
【新闻资讯】查看全部 
橡塑展第一天，带您直击银禧展会现场
2021-04-14 搜料网资讯： 4月13日，CHINAPLAS 2021 国际橡塑展在深圳国际会展中心盛大开幕！银禧科技携各类改性塑料、阻燃剂、电子化学品材料、3D打印材料等产品向现场观众展示，吸引到众多对产 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |