| 牌号简介 About |
|---|
| SABIC® HDPE B5429是一种中分子量高密度聚乙烯共聚物。它通常用于吹塑小尺寸的瓶子。SABIC® HDPE B5429具有很好的韧性、抗应力开裂性（ESCR）、承载强度和加工性能。典型应用。SABIC® HDPE B5429属于多用途吹塑等级。它可以吹塑成家用和工业化学品（如洗涤剂、漂白剂、织物柔软剂、溶剂、油漆等）、汽车用品、食品、洗漱用品和化妆品的容器。它通常也用于其他空心薄壁零件和型材挤压。本产品不适用于任何医药/医疗应用，也不得用于任何医药/医疗应用。 SABIC® HDPE B5429 is a medium molecular weight high density polyethylene copolymer. It is typically used for blow moulding bottles of small sizes. SABIC® HDPE B5429 offers a very good combination of toughness, stress cracking resistance (ESCR), load bearing strength and processability characteristics. Typical applications. SABIC® HDPE B5429 is classified as a multipurpose blow moulding grade. It may be blow moulded into containers for household and industrial chemicals (e.g. detergents, bleach, fabric softeners, solvents, paints, etc.), automotive supplies, foodstuffs, toiletries and cosmetics. It is typically also used for other hollow thin-walled parts and profile extrusions. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
用途：汽车领域的应用;工业应用;容器;型材;瓶子;薄壁部件;
加工条件：型材挤出成型 Profile extrusion
性能特点： 高密度; 共聚物; 抗应力开裂; 韧性好; 易加工; Excellent Processability,Good flexibility,Copolymer,High density,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.954 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
190℃，2.16kg 190℃，2.16kg |
0.30 | g/10min | ISO 1133 |
|
190℃，21.6kg 190℃，21.6kg |
29 | g/10min | ISO 1133 |
|
190℃，5.0kg 190℃，5.0kg |
1.5 | g/10min | ISO 1133 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
10%非离子洗涤剂，模压成型，F50 10% non-ionic detergent, molded, F50 |
40.0 | hr | ASTM D1693B |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
|
-30℃，模压成型 -30 ℃, molded |
kJ/m² | ISO 180-A | |
|
23℃，模压成型 23 ℃, molded |
kJ/m² | ISO 180-A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
|
熔融温度 Melting temperature |
℃ | DIN 53765 | |
|
Enthalpy Change Enthalpy Change |
J/g | DIN 53765 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blow Molding Melt Temperature Blow Molding Melt Temperature |
℃ | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，模压成型 Shaw's D, molded |
ISO 868 | ||
|
拉伸模量 Tensile modulus |
|||
|
2 mm，模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
|
拉伸强度 tensile strength |
ISO 527-2/1BA/50 | ||
|
屈服，2 mm，模压成型 Yield, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
|
断裂，2 mm，模压成型 Fracture, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，2 mm，模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/1BA/50 | |
|
弯曲模量 Bending modulus |
|||
|
2 mm，模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
2 mm，模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部 
宜家与世界冲浪联盟携手合作，致力于采用可回收聚酯纤维的可回收和
2022-08-11 海洋环境保护问题长期以来受到各界的关注，并已开始采取行动。作为世界著名的家具与家具用品品牌，宜家早在2019年就与世界冲浪联盟（WSL）合作，旨在以与海洋密切相关的动态和积 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付