牌号简介 About |
---|
Alcudia2303F是一种低密度聚乙烯级产品,采用高压管技术生产,适用于吹塑或铸膜应用。这种材料具有易加工性和良好的机械和光学性能平衡。它不含任何添加剂。一般包装膜的典型应用。重型袋子。收缩膜具有很高的机械阻力。推荐的熔化温度范围为180至210°C。应为每条生产线优化加工条件。 ALCUDIA® 2303F is a low density polyethylene grade, produced by high pressure tubular technology, suitable for blown or cast film applications. This material offers easy processability and good balance of mechanical and optical properties. It does not contain any additives. TYPICAL APPLICATIONS General packaging film. Heavy duty sacks. Shrink film with high mechanical resistance. Recommended melt temperature range from 180 to 210°C. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.921 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.30 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
> 0.40 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
200 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,200 µm,吹塑薄膜 MD, yield, 200 µ m, blow molded film |
9.00 | MPa | ISO 527-3 |
TD,屈服,200 µm,吹塑薄膜 TD, yield, 200 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,200 µm,吹塑薄膜 MD, fracture, 200 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,200 µm,吹塑薄膜 TD, fracture, 200 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,200 µm,吹塑薄膜 MD, fracture, 200 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,200 µm,吹塑薄膜 TD, fracture, 200 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
200 µm,吹塑薄膜 200 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:200 µm,吹塑薄膜 MD: 200 µ m, blow molded film |
N | ISO 6383-2 | |
TD:200 µm,吹塑薄膜 TD: 200 µ m, blow molded film |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,200 µm,吹塑薄膜 45 °, 200 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
200 µm,吹塑薄膜 200 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 ![]()
大事件!全国将检查PE农膜和塑料袋厂,进厂查台账,持续一个月!
2020-11-24 搜料网资讯: 11月16日,国家市场监督管理总局通知,要求各地市场监督部门开展聚乙烯农用地膜和塑料购物袋生产企业监督检查和产品质量监督抽查工作。并于12月20日之前,向总局质 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |