牌号简介 About |
---|
LEXAN™ 4701R resin是高耐热聚碳酸酯,LEXAN™ 4701R resin是聚碳酸酯树脂的共聚物,用于需要高耐热性的应用。与Lexan 4501相比,该等级具有更高的热性能。 High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
特定体积 Specific volume |
0.830 | cm³/g | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
300℃,1.20kg 300℃,1.20kg |
2.0 | g/10min | ASTM D1238 |
300℃,6.10kg 300℃,6.10kg |
9.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.80 to 1.0 | % | 内部方法 |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
拉伸冲击强度 Tensile impact strength 4 |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
J/kg/℃ | ASTM C351 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance 5 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 80*10*3 sp=62mm |
7 80*10*3 |
8 Type S |
9 120*10*4 mm |
10 钨电极 |
【新闻资讯】查看全部 ![]()
中国产业调整影响五大通用塑料供应格局
2017-03-15 综合分析,近年来,我国五大通用塑料――PE、PVC、PP、ABS、PS的供应格局呈现出很大的变化,这跟中国产业结构调整息息相关。其中,PE在五大通用塑料的产能占比从2011年的第二位降至2015年的第三位,而PVC逐渐去产能化,在五大通用塑料产能中的占比大幅下降。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |