牌号简介 About |
---|
PA 6,30%玻璃纤维,注塑成型,提高冲击强度,热老化稳定 Durethan® BKV130H3.0 000000 DUS008 (Dry) PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV130H3.0 000000 DUS008 PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV130H3.0 000000 DUS008 PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.37 | g/cm³ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
9000 | MPa | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
160 | MPa | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
4.0 | % | |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
8000 | MPa | |
弯曲强度 bending strength 2 |
|||
23℃ 23℃ |
MPa | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ||
弯曲应变 Bending strain 3 |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
熔融温度 Melting temperature 4 |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
2. 2.0 mm/min |
3. 2 mm/min |
4. 10°C/min |
【新闻资讯】查看全部
石化行业“碳”讨高质量发展新思路
2021-10-13 搜料网资讯: 双碳、双控背景下,石化化工行业的高质量发展面临着严峻的挑战。在9月24日举办的以绿色低碳、提质增效为主题的石化化工行业十四五高质量发展报告会上,石油和化学 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |