| 牌号简介 About |
|---|
| Lexan 943x树脂Lexan 943x是一种紫外线稳定介质流动冲击改性注射成型（IM）等级。该树脂提供基于无溴、无氯FR系统的UL94 V0@1.5毫米阻燃性、低温延展性特征和良好的加工性能，与标准PC相比，IM循环时间更短。LEXAN™ 943X resin是一种可用于各种不透明颜色的产品，可能是广泛应用于应用范围。 LEXAN 943X is a UV stabilized medium flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN 943X resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications. |
产品描述 Product Description
用途：通用;
颜色：可用颜色,不透明
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 成型周期快; 流动性中等; 机械强度好-延展; 阻燃; 防火阻燃等级5VA; 冲击性能好; 耐候抗UV; 易加工; Weather resistance is good,Excellent Processability,High impact resistance,Ductility,Quick molding cycle,Halogen free,Flame Characteristics,Moderate liquidity,V-0,5VA
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.18 | g/cm³ | ASTM D792 |
|
密度 Density |
1.19 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
10 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
9.00 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
TD：3.2 mm TD：3.2 mm |
0.40 to 0.80 | % | 内部方法 |
|
MD：3.2 mm MD：3.2 mm |
% | 内部方法 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
|||
|
屈服，50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
|
-30℃ -30℃ |
ISO 180/1U | ||
|
23℃ 23℃ |
ISO 180/1U | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 9 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
|||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：23~80℃ TD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
MD：23~80℃ MD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电强度 Dielectric strength |
|||
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.051 in/min |
| 5 0.079 in/min |
| 6 Yield |
| 7 80*10*3 sp=62mm |
| 8 80*10*3 |
| 9 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
北欧化工将提高化学回收产物的质量，并为此建立新工厂
2022-04-29 北欧化工表示，计划在瑞典Stenungsund建立一个工厂，对化学回收塑料生产的裂解油进行升级。 Axens表示，根据授权协议，北欧化工将使用Axens的Rewind Mix工艺技术。该公司将提供工艺设计 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付