牌号简介 About |
---|
Hysol® KL-G900HP环氧模塑料不含溴、锑或磷阻燃剂。该材料设计用于在260°C回流温度下达到JEDEC 1级要求。Hysol® KL-G900HP为大型QFN包提供了增强的可靠性性能。KL-G900HP在3.175mm厚度下符合UL 94 V-0可燃性。产品优点绿色产品低扫线成型低翘曲 Hysol® KL-G900HP epoxy molding compound contains no bromine, antimony or phosphorus flame retardant. This material is designed to achieve JEDEC Level 1 requirements, at 260°C reflow temperature. Hysol® KL-G900HP offers enhanced reliability peformance for large QFN packages. KL-G900HP meets UL 94 V-0 Flammability at 3.175mm thickness. Product Benefits Green product Low wire sweep molding Low warpage |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.99 | g/cm³ | |
螺旋流动长度 Spiral flow length 2 |
82.0 | cm | |
收缩率 Shrinkage rate |
|||
MD MD |
0.030 | % | |
吸水率 Water absorption rate |
|||
85℃,7days,85% RH 85℃,7days,85% RH |
0.18 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
|||
25℃ 25℃ |
25100 | MPa | |
弯曲强度 bending strength |
|||
25℃ 25℃ |
MPa | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
< 100℃ < 100℃ |
cm/cm/℃ | ||
> 100℃ > 100℃ |
cm/cm/℃ | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
UL 94 | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
胶凝时间 Gelation time |
|||
175℃ 175℃ |
min | ||
贮藏期限 Storage period |
|||
5℃ 5℃ |
month |
备注 |
---|
2、熔体温度: 175°C |
【新闻资讯】查看全部
碳中和现代产业学院专委会成立
2022-08-24 扫描上图二维码,可以免费下载 搜料 APP 8月18日,碳中和的现代产业学院建设研讨会暨碳中和的现代产业学院专委员会成立大会在京举行。 在中国现代产业学院协同创新平台理事会的领 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |