牌号简介 About |
---|
SABIC PP化合物2605/1是一种填充矿物的改性聚丙烯。典型的材料特性包括具有低密度的良好冲击刚度平衡。这种材料的最佳气味低,低排放和良好的油漆性能。典型应用包括喷漆的汽车内部零件,如装饰件和仪表板。SABIC PP化合物2605/1是指定的汽车等级。 SABIC® PPcompound 2605/1 is a mineral filled modified polypropylene. Typical material properties include an excellent impact stiffness balance with a low density. This material was optimized for low smell, low emission and good paintability. Typical applications include painted automotive interior parts such as trims and dashboards. SABIC® PPcompound 2605/1 is a designated automotive grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.960 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
230℃,2.16kg 230℃,2.16kg |
5.0 | g/10min | ISO 1133 |
230℃,5.0kg 230℃,5.0kg |
23 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
24 hrs 24 hrs |
1.2 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,注塑成型 23 ℃, injection molding |
无断裂 | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-40℃,注塑成型 -40 ℃, injection molding |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/4A | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-4A | |
0℃,注塑成型 0 ℃, injection molding |
kJ/m² | ISO 180-4A | |
23℃,注塑成型 23 ℃, injection molding |
ISO 180/4A | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM D696 | ||
-30 到 30℃ -30 to 30 ℃ |
cm/cm/℃ | ASTM D696 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ASTM D696 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/5/50 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/5/50 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ISO 527-2/5/50 | |
拉伸应变 Tensile strain |
|||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ISO 527-2/5/50 | |
弯曲模量 Bending modulus 2 |
|||
注塑成型 injection molding 2 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 I (三点负荷) |
【新闻资讯】查看全部
山东省化专办与中国石化联合会签约战略合作!
2021-06-07 搜料网资讯: 2021年6月3日,2021中国化工园区与产业发展论坛在山东烟台隆重召开。本次会议由中国石油和化学工业联合会、山东省化工专项行动办公室(以下简称山东省化专办)、山东 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |