警告:此材料的状态为“商业:限量发行”。此材料的数据最近尚未验证。在指定此等级之前,请联系RTP公司以获取当前信息。RTP 301 EM是一种10%玻璃纤维增强聚碳酸酯,具有高冲击强度和易于成型的特点。它具有良好的尺寸稳定性和提高耐热性和强度的基础树脂。保持自熄特性。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 301 EM is a 10% glass fiber reinforced polycarbonate formulated for high impact strength and easy molding. It has good dimensional stability and improved heat resistance and strength over the base resin. Self-extinguishing FR characteristics are maintained. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.30 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.12 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
6.4mm 6.4mm |
210 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
6.4 mm 6.4 mm |
2100 | J/m | ASTM D4812 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.6 mm,RTP Tested 1.6 mm,RTP Tested |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
再生聚丙烯行业展开遇瓶颈如何破重围
2016-11-29 再生聚丙烯行业经过近30年的发展,发展瓶颈凸显。2016年再生聚丙烯整体运行偏弱,在下游刚需拖累下相关运行指标长期处在偏低水平。此格局导致上下游资金周转不畅,从而进一步加剧业者操盘难度,导致部分业者长期处于低负荷开工维持工人状态。本文将具体阐述一下再生聚丙烯行业发展现状。 进口监管力度从严 环保整顿如影随形 近几年,再生塑料行业一直弥漫着环保整顿的气氛,自2013年之后,伴随监管力度的逐渐加大,对行业的影响也是不言而喻。纵观2016年环保整顿行动屡出不穷。宿 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |