牌号简介 About |
---|
Halar® 350LC是一种三氟氯乙烯-聚乙烯材料,。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:挤出。 Halar® 350LC的主要特性有: 阻燃/额定火焰 中等粘度 Halar® 350LC is an Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion. Important attributes of Halar® 350LC are: Flame Rated Medium Viscosity |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.68 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
275℃,2.16kg 275℃,2.16kg |
3.0 到 6.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
2.5 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡 balance |
< 0.10 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃,3.2mm -40℃,3.2mm |
210 | J/m | ASTM D256 |
23℃,3.2mm 23℃,3.2mm |
ASTM D256 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746A | |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
熔融温度 Melting temperature |
℃ | ASTM D3418 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
比热 specific heat |
|||
23℃ 23℃ |
J/kg/℃ | ASTM D3418 | |
导热系数 Thermal conductivity coefficient |
|||
40℃ 40℃ |
W/m/K | ASTM C177 | |
结晶热 Crystallization heat |
J/g | ASTM D3418 | |
热稳定性 thermal stability |
|||
1%质量损失,N2 1% mass loss, N2 |
℃ | TGA | |
融合热量 Fusion heat |
J/g | ASTM D3418 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity 4 |
|||
23℃ 23℃ 4 |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
23 ℃,3.2 mm 23 ℃,3.2 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23 ℃,1 MHz 23 ℃,1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus 2 |
|||
23℃ 23℃ 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 2 |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
|||
23℃ 23℃ 3 |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
ASTM D1894 | ||
与自身 - 静态 With oneself - static |
ASTM D1894 | ||
泰伯耐磨性 Taber abraser |
|||
1000 周期,500 g,CS-17 转轮 1000 cycles, 500 g, CS-17 wheels |
mg |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.098 in/min |
4 50% RH |
【新闻资讯】查看全部
2018年上半年科莱恩销售额到达33.89亿法郎
2018-08-01 ●销售额达到33.89亿瑞士法郎,以当地货币计算增长7% ● 扣除特殊项的息税、折旧及摊销前利润(EBITDA)大幅增长9% ● 扣除特殊项的EBITDA利润率上升至15.5% ● 净利润增长38%,达到2.11亿瑞士法郎 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |