牌号简介 About |
---|
Clearflex FG 106 A是一种含抗氧化剂的六烯共聚物线性低密度聚乙烯(C6-LLDPE),适用于吹塑薄膜挤出。使用Clearflex FG 106 A制造的薄膜具有优良的光学性能(雾度和光泽度)、最佳的密封性能和高机械性能。主要应用Clearflex FG 106 A由于添加剂的高纯度和低扩散性,特别适用于食品包装等应用。Clearflex FG 106 A被推荐用于农业薄膜的生产,吹塑拉伸薄膜与低密度聚乙烯共挤或混合。 Clearflex FG 106 A is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion. Film manufactured with Clearflex FG 106 A are characterised by excellent optical properties (haze and gloss), optimum sealing performances and high mechanical properties. Main Applications Clearflex FG 106 A thanks to high purity and low diffusivity of the additives, is particularly suitable in applications such as food packaging. Clearflex FG 106 A is recommended for the production of agricultural film, blown stretch film coextruded or blended with LDPE. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.1 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
动态,吹塑薄膜 Dynamic, blow molded film |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
薄膜厚度 film thickness |
10 to 50 µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ISO 7765-1/A | |
撕裂强度 tear strength 2 |
ISO 6383-2 | ||
MD,25 µm MD,25 µm |
kN/m | ISO 6383-2 | |
TD,25 µm TD,25 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部
埃克森美孚工厂爆炸 大火黑烟不时,37人受伤,公司再次面临巨额赔款
2019-08-05 7月31日周三下午, 埃克森美孚 位于德克萨斯州贝敦的烯烃工厂发生火灾,造成37人受伤,随后股票暴跌。 火灾发生在大约上午11点07分(当地时间)位于休斯敦以东约25英里(40公里)贝 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |