牌号简介 About |
---|
MALEX 01EFR002 - 4229是一种中等粘度聚碳酸酯(PC)树脂(UL94v2),含有一种释放剂,以确保易于加工,用于注塑成型。该产品有黑色(MALEX 01EFR002-8229)可供选择,但也可根据要求提供其他颜色。它们结合了高机械要求的刚性、热性能和电气性能以及优异的耐化学性和尺寸稳定性应用MALEX 01EFR002 - 4229旨在用于电气部件和机械部件的注塑成型。系统,如:电器元件照明系统技术部分 MALEX 01EFR002 - 4229 is a medium viscosity polycarbonate (PC) resin (UL94 V2) and contains a release agent to ensure easy processing, intended for injection moulding. The product is available in black (MALEX 01EFR002 - 8229) but other colours can be provided on request They combine high mechanical requiring rigidity, thermal and electrical properties with excellent chemical resistance and dimensional stability APPLICATIONS MALEX 01EFR002 - 4229 is intended for the injection moulding of electrical components and mechanical systems, such as: Electrical appliance components Lighting system Technical parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
12 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.35 | % | DIN 53495 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2350 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179/1eU | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
我国迷信家创造新型形状记忆塑料
2016-01-12 一张塑料薄片放置到60摄氏度的热水里,短短几秒钟,塑料薄片收缩变形成一只“千纸鹤”。 这是浙江大学化学工程与生物工程学院谢涛教授课题组最新研发的一种新型形状记忆塑料,它能多次“植入”复杂形状记忆,遇热即展现多样形变。相关论文于9日发表在《科学》杂志子刊《科学进展》上。 形状记忆塑料是一类能够暂时固定在临时形状,受到外界刺激后回复到初始形状的智能材料,在柔性电子、生物医学和航空航天等领域展示了越来越广的应用前景。 谢涛介绍,研究团队在设计新型形 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |