Jampilen HP550J是一种聚丙烯均聚物,特别适用于热成型片材、薄膜纱和单丝的挤出。这一等级结合了出色的加工性能和良好的机械性能。Jampilen HP550J是专为生产薄膜而设计的,这些薄膜可以被转换成用于编织的拉伸带。用于生产地毯衬垫、袋子、工业织物、垫子和人造草的纺织薄膜纱线,但尼尔数不超过1100至1200。细旦数在3000到28000之间的薄膜纱用于打捆机捆绳、包装捆绳和绳索。Jampilen HP550J适用于食品接触。 "Jampilen HP550J" is a polypropylene homopolymer particularly suitable for the extrusion of sheet for thermoforming, film yarn and monofilament. This grade combines outstanding processability with good mechanical properties. "Jampilen HP550J" is designed for the production of films that can be converted into stretched tapes for weaving applications. Textile film yarns with a denier count of not more than 1100 to1200 are used for the production of carpet backings, bags, industrial fabrics, mats and artificial grass. Film yam with a denier count ranging from 3000 to 28000 is used for baler twines, packaging twines and ropes. "Jampilen HP550J" is suitable for food contact. Features: Good processability Good mechanical properties Homopolymer Typical Applications: Stiff sheet for high quality therinoformings such as vending cups, packaging for dairy products and trays for fruit, biscuits and chocolates Film yam, rafia, tapes, strapping Carpet backings, bags, industrial fabrics, mats and artificial grass Baler twines, packaging twines and ropes Brush and broom filling and technical applications Nets for various purposes |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
3.2 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
55 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
94.0 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
156 | ℃ | ASTM D1525 2 |
加速干燥箱老化 Accelerate oven aging |
|||
150℃ 150℃ |
hr | ASTM D3012 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
2017年三季度巴斯夫销售额和收益明显增长
2017-10-25 2017年第三季度: ・ 销售额达到153亿欧元(上升9%) ・ 不计特殊项目的息税前收益达到18亿欧元(上升16%) ・ 每股收益为1.45欧元(上升49%),调整后每股收益1.40欧元(上升27%) ・ 运营活动提供的现金达到38亿欧元(上升52%),自由现金流28亿欧元 2017年全年展望: ・ 巴斯夫继续预期销售额、不计特殊项目的息税前收益和息税前收益都将显著增长 德国路 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |