| 牌号简介 About |
|---|
| LD7001A是在高压釜反应器中用高压工艺生产的低密度聚乙烯。为生产挤出薄膜而开发。具有较高的机械强度和冲击强度，良好的加工性能，较高的抗静电性能和良好的收缩性能。添加：防滑剂应用：共挤收缩膜。工艺：薄膜挤出的推荐工艺条件约为200-220°C。最佳工艺条件将根据所用设备的类型而变化，不能作为性能保证。 LD7001A is a Low Density Polyethylene produced by High Pressure Process, in Autoclave reactor. Developed for the manufacturing of extruded films. It has high mechanical and impact strength, good processability, high ESCR and good shrinkage. Additivation: Antiblocking Slip agent Application: Coextruded and shrink films. Process: Recommended processing conditions for film extrusion about 200 - 220 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
产品描述 Product Description
用途：薄膜;
加工条件：共挤薄膜
性能特点： 抗结块性; 高光滑性; 冲击性能好; 收缩性低; 低密度; 抗应力开裂; 易加工; Excellent Processability,High impact resistance,Smoothness,High anti-blocking,Low contractility,Low density,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.921 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.34 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，断裂，70 µm，吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
25.0 | MPa | ASTM D882 |
|
TD，断裂，70 µm，吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
25.0 | MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂，70 µm，吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
320 | % | ASTM D882 |
|
TD，断裂，70 µm，吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
|||
|
70 µm，吹塑薄膜 70 µ m, blow molded film |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
TD，70 µm，吹塑薄膜 TD, 70 µ m, blow molded film |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60°，70.0 µm，吹塑薄膜 60 °, 70.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
70.0 µm，吹塑薄膜 70.0 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
|
【新闻资讯】查看全部
武汉乙烯工程晋级改造 年产能将升至110万吨
2017-10-25 记者昨日从中韩石化武汉乙烯获悉，武汉乙烯将在现有年产80万吨乙烯的基础上，通过挖潜、改造，将乙烯生产能力扩至年产110万吨。 据悉，武汉乙烯脱瓶颈改造项目总投资42.7亿元，以武汉乙烯目前核心三机基础不动，主要塔壳体不动、内件改造为前提，在现有年产乙烯80万吨的基础上，改造4套装置、新建两套装置和公用工程系统改造等。 楚天都市报记者获悉，该项目计划于2018年9月开工，2020年建成投产。届时将通过进一步扩大产能，增产市场需要的高附加值化工产品，发挥现有装置 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |