牌号简介 About |
---|
J-320C是以乙烯含量为共聚单体的冲击嵌段共聚物。该等级设计用于在常规注射成型设备中加工。J-320C具有良好的低温抗冲击性能和较高的刚度。它具有广泛的性能,可用于从工业用品到盖封基树脂。 Description J-320C is impact block copolymer with ethylene content as co-monomer. This grade is designed to be processed in conventional Injection molding equipment. J-320C shows good impact resistance at low temperature and has also high stiffness. It has broad range of property, and is used from industrial supplies to cap & closure base resin. Applications Cap and Closure Container, Toys etc |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
4.0 | g/10min | ASTM D1238,ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
28.4 | MPa | ASTM D638 |
屈服 yield |
27.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 100 | % | ASTM D638 , ISO 527-2 |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-10℃ -10℃ |
J/m | ASTM D256 | |
-10℃ -10℃ |
J/m | ISO 180 | |
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
受疫情影响!巨化股份终止重组,放弃入股浙江石化
2021-06-12 搜料网资讯: 6月10日晚间,巨化股份发布公告称,因交易双方短期内难以就交易方案 核心 条款达成一致意见,公司决定终止重大资产重组事项,放弃入股浙江石化,并将于2021年6月17日 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |