| 牌号简介 About |
|---|
| N02J-00是一种低熔融流速、高抗冲共聚聚丙烯，适用于片材挤出和厚壁注射成型应用。它提供了一个优越的平衡刚度和冲击强度的热成型物品，其中冷冻到微波性能是必需的。典型的应用包括家电、复合材料、消费品、家庭用品和刚性包装。好处包括提高室温和低温冲击以及增强刚度。该材料符合21 CFR 177.1520中规定的美国食品药品管理局的要求。 N02J-00 is a low melt flow rate, high impact copolymer polypropylene for sheet extrusion and thick wall injection molding applications. It offers a superior balance of stiffness and impact strength for thermoformed articles where freezer to microwave performance is required. Typical applications include appliances, compounding, consumer products, housewares, and rigid packaging. Benefits include enhanced room temperature and low temperature impact and enhanced stiffness. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
产品描述 Product Description
用途：家用货品;厚壁配件（部件）;片材;硬包装;消费品应用领域;复合;热成型应用;电器用具;
加工条件：热成型 Thermo forming
性能特点： 抗冲共聚物; 流动性低; 冲击性能好; 食品接触; Low liquidity,High impact resistance,Food contact compliance,Impact copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.900 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
2.0 | g/10min | ASTM D1238 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-20℃，注塑成型，Area -20 ℃, injection molding, Area |
7.10 | kJ/m² | ASTM D256 |
|
-20℃，注塑成型 -20 ℃, injection molding |
75 | J/m | ASTM D256 |
|
23℃，注塑成型 23 ℃, injection molding |
No Break | ASTM D256 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
|
-20℃，注塑，韧性破坏 -20 ℃, injection molding, toughness failure |
ASTM D3763 | ||
|
23℃，注塑，韧性破坏 23 ℃, injection molding, toughness failure |
ASTM D3763 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60°，注塑成型 60 °, injection molding |
ASTM D2457 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength 2 |
|||
|
断裂，注塑成型 Fracture, injection molding 2 |
MPa | ASTM D638 | |
|
屈服，注塑成型 Yield, injection molding 2 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 2 |
|||
|
断裂，注塑成型 Fracture, injection molding 2 |
% | ASTM D638 | |
|
屈服，注塑成型 Yield, injection molding 2 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
1% 正割，注塑成型 1% cut, injection molding |
MPa | ASTM D790-A | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
|
【新闻资讯】查看全部 
海湾合作国家塑料制品市场将于2014-2023间年度增长8%
2021-06-20 搜料网资讯： 海湾合作国家(GCC)包括沙特阿拉伯、科威特、阿拉伯联合酋长国、卡塔尔、巴林和阿曼的塑料制品市场预计将在2014-2023年间达到8.3%的年度复合增长率。根据市场研究报，其 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付