| 牌号简介 About |
|---|
| 概述：WL-30是一种玻璃纤维和聚四氟乙烯填充改性PPS化合物，具有低摩擦和耐磨性。颜色：布莱克 Outline: WL-30 is a glass fiber and poly tetra fluoro ethylene filled modified PPS compound that provides low friction and wear resistance. Color: Black |
产品描述 Product Description
颜色：黑色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 耐磨; 低摩擦系数; Low coefficient of friction,Good wear resistance,V-0
填料：PTFE/玻璃纤维
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.68 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage rate |
ASTM D955 | ||
|
MD MD |
0.25 | % | ASTM D955 |
|
TD TD |
1.0 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.050 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
60 | J/m | ASTM D256 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM D696 | ||
|
MD：-30~90℃ MD：-30~90℃ |
1/℃ | ASTM D696 | |
|
TD：-30~90℃ TD：-30~90℃ |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
1.6 mm 1.6 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
0.80 mm 0.80 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
泊松比 Poisson's ratio |
|||
|
摩擦系数 friction coefficient |
ASTM D1894 | ||
|
与钢 - 动态 Steel - Dynamic |
ASTM D1894 | ||
|
与钢 - 静态 Steel - Static |
ASTM D1894 | ||
|
断裂弯曲伸长率 Elongation at break and bending |
% | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
零件坐标系的意义
2015-12-08 三坐标测量仪，顾名思义就是利用点的三维坐标值进行测量的仪器。既然要用到空间各个点的坐标值，就必然要有坐标系的存在。在测量时，坐标系的建立的必不可少的，那么在测量零件时建立的坐标系具有哪些意义呢? 1.找正零件。零件放置在工作台上时，不可能与三坐标测量仪的软件坐标系完全重合，如果不建立零件坐标系的话，就无法进行测量，或者在测量的过程中会因投影平面等问题出现误差，所以要根据零件的基准来建立零件坐标系，也就是“找正零件”。 2.建立零件基准。在测量距离、观察坐标位 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付