| 牌号简介 About |
|---|
| Eastar共聚酯DN004在γ和ETO灭菌后进行了FDA/ISO 10993和USP六级生物评价试验。Eastar共聚酯是一种非常透明的聚合物，具有优异的冲击强度、耐化学性、尺寸稳定性和低收缩率。DN004含有脱模剂。本产品已通过绿色卫士室内空气质量认证。Greenguard室内空气质量认证标志是通过Greenguard环境研究所（GEI）许可使用的注册认证标志。GEI是一个行业独立的非盈利组织，负责监督Greenguard认证计划。Greenguard认证计划是一个行业独立的第三方测试计划，用于室内环境的低排放产品和材料。欲了解更多关于GEI的信息，并获得Eastman共聚酯的可打印证书，请访问www.greenguard.org。在制造商类别下选择Eastman Chemical Company，然后单击搜索以显示我们的产品列表。 Copolyester DN004 has been tested for FDA/ISO 10993 and USP Class VI Biological Evaluation testing after Gamma and EtO sterilization. Eastar™ copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar™ DN004 copolyesters are the toughest materials for the cosmetics and personal care packaging applications. It's very shatter resistant and offers excellent chemical resistance. DN004 contains a mold release. This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED The GREENGUARD INDOOR AIR QUALITY CERTIFIED Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products. |
产品描述 Product Description
用途：医疗/护理用品;眼镜;体育用品;电器用具;家电部件;包装;镜架;玩具;牙刷柄;文具;个人护理;化妆品包装;地板保养/维修;
颜色：自然色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 含脱模剂; 尺寸稳定性好; 耐化学性; 透光性好; 辐射消毒; 冲击性能好; 收缩性低; 电子束消毒; Good Clarity,High impact resistance,Good Dimensional Stability,Low contractility,E-beam disinfection,Good stripping performance,Radiation disinfection,Solvent resistance,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.23 | g/cm³ | ASTM D792 |
|
密度 Density |
1.23 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.20 to 0.50 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.13 | % | ASTM D570 |
|
23℃，24hr 23℃，24hr |
0.13 | % | ISO 62 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-40℃ -40℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
ASTM D256 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
|
-40℃ -40℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4218 | ||
|
-40℃ -40℃ |
ASTM D4218 | ||
|
23℃ 23℃ |
ASTM D4218 | ||
|
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
|
-40℃，能量到力量峰值 -40 ℃, energy to peak strength |
J | ISO 6603-2 | |
|
23℃，能量到力量峰值 23 ℃, energy to peak strength |
J | ISO 6603-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ISO 306/A | |
|
-- -- |
℃ | ISO 306/B | |
|
比热 specific heat |
DSC | ||
|
60℃ 60℃ |
J/kg/℃ | DSC | |
|
240℃ 240℃ |
J/kg/℃ | DSC | |
|
导热系数 Thermal conductivity coefficient |
|||
|
23℃ 23℃ |
W/m/K | ASTM C177 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电强度 Dielectric strength 4 |
|||
|
23℃ 23℃ 4 |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
23 ℃，1 kHz 23 ℃，1 kHz |
ASTM D150 | ||
|
23 ℃，1 MHz 23 ℃，1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
23℃，1 kHz 23℃，1 kHz |
ASTM D150 | ||
|
23℃，1 MHz 23℃，1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
mm/min | UL 746 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Transmittance |
ASTM D1003 | ||
|
总计 total |
% | ASTM D1003 | |
|
Regular Regular |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃，4 mm Fracture, 23 ℃, 4 mm |
MPa | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
屈服，23℃，4.00 mm Yield, 23 ℃, 4.00 mm |
MPa | ISO 527-2 | |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃，4 mm Fracture, 23 ℃, 4 mm |
% | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
屈服，23℃，4 mm Yield, 23 ℃, 4 mm |
% | ISO 527-2 | |
|
屈服，23℃ Yield, 23 ℃ |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
23℃，4 mm 23℃，4 mm |
MPa | ISO 178 | |
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
23℃，4 mm 23℃，4 mm |
MPa | ISO 178 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
| 3 500 V/sec, 方法A（短时间） |
|
【新闻资讯】查看全部 
益德新材料---石墨烯改性纤维
2020-09-24 搜料网资讯： 宁波益德新材料有限公司的前身是余姚章盛塑业，已有二十余年的历史。公司主要从事军工、电子电器、纺织与纺机、汽车等领域的产品材料，如炸 药箱、通信接线盒、纺 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付