牌号简介 About |
---|
ADIPRENE L 300是一种基于聚醚的液体聚氨酯预聚物,可通过传统的手工和机械混合技术进行加工。当使用4,4’-亚甲基双[2氯苯胺]或Caytur 21da氨基甲酸酯固化剂固化时,Adiprene L 300可在88-92硬度范围内生产高质量的弹性体。这些坚韧、高弹性的弹性体具有许多独特的特点:优异的低温弹性、优异的耐磨性、良好的水解稳定性、良好的压缩永久性。阿迪普林L 300的性能表明其可用于小辊、牵引齿轮和喷涂等应用。在许多情况下,通过减少脱模时间来提高生产率,阿迪普林L 300和MBCA混合物的相对较短的工作寿命可以显著节省处理器。 ADIPRENE L 300 is a polyether-based liquid urethane prepolymer which is readily processable by conventional hand and machine mixing techniques. ADIPRENE L 300 produces high quality elastomers in the 88-92 durometer A hardness range when cured with 4,4'-Methylene-bis[2Chloroaniline] or CAYTUR® 21DA urethane curative. These tough, highly resilient elastomers have many unique features: Excellent low-temperature flexibility Excellent abrasion resistance Good hydrolytic stability Good compression set resistance The properties of ADIPRENE L 300 suggest its use in applications such as small rolls, draft gears, and spraying. The relatively short working life of mixes of ADIPRENE L 300 and MBCA can, in many cases, effect significant savings for the processor by increasing production rates via reduced demolding times. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
90 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
7.07 | MPa | ASTM D412 |
300% 应变 300% strain |
13.8 | MPa | ASTM D412 |
拉伸强度 tensile strength |
29.0 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
NBS NBS |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
100℃ 100℃ |
hr | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability |
|||
85 ℃ 85 ℃ |
min | ||
后固化时间 Post curing time |
|||
100℃ 100℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
蔚来停产5天背后:芯片进口率达90% 国产芯片如何破局?
2021-04-01 搜料网资讯: 人要心,车也要芯。缺了芯片的车,还好造吗? 继华为被卡脖子之后,国产汽车也遭遇了芯片危机。 造车新势力蔚来(NIO)近日对外宣布,由于芯片短缺,公司决定自2 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |