牌号简介 About |
---|
SARANEX™ 23P共挤阻挡膜是为有限使用的防护服而设计的多层膜。它含有道撒兰阻隔树脂,有2.0密耳,中等滑度,天然色,TX,宽度从10到62英寸(250毫米到1570毫米)。一般特性:产量:13500平方英寸/磅(19.2平方米/千克)厚度:2.0密耳(51微米)宽度:10-62英寸。(254-1575 mm)颜色:天然处理:Tx(未处理) SARANEX™ 23P Coextruded Barrier Film is a multi-layer film designed for limited use protective garments. It contains Dow SARAN™ barrier resin, and is available as 2.0 mil, medium slip, natural color, TX, in widths from 10 to 62 inches (250 mm to 1570 mm). General Characteristics: Yield: 13,500 sq in./lb (19.2 m²/kg) Thickness: 2.0 mil (51 µm) Width: 10 - 62 in. (254 - 1575 mm) Color: Natural Treat: TX (untreated) |
技术参数 Technical Data | |||
---|---|---|---|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | ASTM D374 |
薄膜厚度 film thickness |
2.0 mil (51 µ | ||
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
193 | MPa | ASTM D882 |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
221 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
24.1 | MPa | ASTM D882 |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
氧气传输速率 Oxygen transfer rate |
|||
23℃,50% RH,51 µm 23℃,50% RH,51 µm |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
38℃,90% RH,51 µm 38℃,90% RH,51 µm |
g/m²/24 hr | ASTM F1249 | |
热封强度 Heat sealing strength 2 |
内部方法 | ||
MD MD |
N/m | 内部方法 | |
TD TD |
N/m | 内部方法 | |
用量 dosage |
|||
50.8 µm 50.8 µm |
m²/kg | ASTM D4321 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1 秒预热,1 秒保压,30 psi(2.1 巴),350°F (177°C) |
【新闻资讯】查看全部
巴斯夫提高资料品质,助力韩国熔喷无纺布制造商开辟业务新领域
2018-09-10 Irgatec®能够提高聚丙烯熔喷无纺布材料的透气性和长期热稳定性 2018年9月6日―韩国聚丙烯(PP)熔喷无纺布料制造商 --韩国无 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |