陶粒堆肥树脂是可再生的、生态良好的石油基塑料产品替代品,替代了传统塑料中使用的几乎100%的石油基添加剂。陶粒堆肥树脂使用的聚合物和添加剂来自淀粉和其他可再生资源化学。这些成分在最先进的复合设备上小心地混合在一起。所有陶瓷可堆肥树脂,包括可堆肥1000,在美国和欧洲被认证为可生物降解和可堆肥,符合BPI(可生物降解产品协会www.bpiworld.com)可堆肥性标准(ASTM6400D99,ASTM6868)和欧洲生物塑料标准(EN13432)。堆肥1000被设计成具有良好的韧性、刚度和加工性的平衡。可堆肥1000可在现有的传统电动和液压往复螺杆注塑机上加工。有关加工和材料干燥指南,请参阅我们的加工指南。这可以在www.cereplast.com上找到。 Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product, replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding euipments. All Cereplast Compostables® resins, including Compostable 1000, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www..bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432). Compostable 1000 has been designed to have an excellent balance of toughness, rigidity and processability. Compostable 1000 can be processed on existing conventional electric and hydraulic reciprocating screw injection molding machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ASTM D792-A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
5.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
38.4 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
10 | % | ASTM D638 |
弯曲模量 Bending modulus |
3260 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
J | ASTM D5420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
科莱恩任命Conrad Keijzer为首席执行官
2020-12-11 搜料网资讯: 中国上海/瑞士穆顿兹,2020年12月9日科莱恩,专注、可持续、创新的特种化学公司,今日宣布,Conrad Keijzer将就任科莱恩新的首席执行官。董事会在昨晚的会议中通过了此次 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |