牌号简介 About |
---|
DOWLEX™ 2355聚乙烯树脂是一种乙烯-辛烯共聚物,由陶氏化学公司专有溶液法生产。具有独特的分子结构,侧链分布可控,具有优异的抗应力开裂性能,并具有很好的长期静液强度。加工性:加工DOWLEX™ 2355聚乙烯树脂的典型挤压温度范围为190至230°C。使用反向温度曲线可能有利于某些类型的加工设备。有关更多信息,请参阅我们的挤出指南。应用:热水和冷水系统用管道,例如:地板加热墙加热/冷却天花板冷却散热器连接热水/冷水分配热回收系统太阳能电池板符合:欧盟,2011年第10号,美国食品和药物管理局21 CFR 175.105(c)(5)美国食品和药物管理局21 CFR 177.1520(c)3.2a(有限制)参考法规细节。 DOWLEX 2355 Polyethylene Resin is an ethylene-octene copolymer, produced in the proprietary solution process of The Dow Chemical Company. It has a unique molecular structure with a controlled side chain distribution, which provides excellent stress crack resistance properties combined with very good Long Term Hydrostatic Strength. Processability: Typical extrusion temperatures for processing of DOWLEX 2355 Polyethylene Resin range from 190 to 230° C. The use of a reverse temperature profile may be beneficial on certain types of processing equipment. For further information, see our Extrusion Guideline. Applications: Pipes for hot and cold water systems, e.g.: floor heating wall heating/cooling ceiling cooling radiator connections warm / cold drinking water distribution heat recovery systems solar panels Complies with: EU, No 10/2011 U.S. FDA 21 CFR 175.105(c)(5) U.S. FDA 21 CFR 177.1520(c)3.2a (with Restrictions) Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.931 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | |
190℃,5.0kg 190℃,5.0kg |
2.3 | g/10min | |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,10%乳化剂 50 ℃, 10% emulsifier |
> 8760 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
399 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
% | ||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ||
弯曲模量 Bending modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:20~70℃ MD:20~70℃ |
1/℃ | DIN 53752 | |
导热系数 Thermal conductivity coefficient |
|||
60℃ 60℃ |
W/m/K | DIN 52612 | |
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness 2 |
|||
邵氏 D,2.00 mm Shore D, 2.00 mm 2 |
ISO 868 |
备注 |
---|
2、Compression Molded |
【新闻资讯】查看全部
DPM推出三种高功能3D打印资料
2017-03-24 近日,杜邦高性能材料公司推出了一些列基于现有聚合物的新的3D打印材料。在芝加哥的添加剂制造用户组会议上,其介绍了包括Dupont Hytrel热塑性弹性体、DuPont Zytel尼龙和DuPont Surlyn离聚物的三种新材料。 现在,三种塑料材料已经适用于3D打印机,为用户提供高性能和可靠的3D打印长丝。杜邦高性能材料公司(Dupont Performance Materials)表示,使用其新灯丝,用户将能够享受3D打印的全部优势,包括更大的设计自由度、轻重量、减少 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |