牌号简介 About |
---|
PRE-ELEC® PE 1291是一种基于PE-HD的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。PRE-ELEC® PE 1291具有良好的机械性能平衡,易于挤压。典型的应用包括吹塑瓶,容器和罐或单或共挤管和片材。 PRE-ELEC® PE 1291 is a conductive thermoplastic compound based on PE-HD. The electrical conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PE 1291 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include blow moulded bottles, containers and canisters or mono- or co-extruded pipes and sheets. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ASTM D792 |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,10.0kg 190℃,10.0kg |
0.70 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
6.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
2.5 to 3.5 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ISO 868 | ||
拉伸强度 tensile strength 2 |
|||
流量,屈服 Flow rate, yield |
MPa | ISO 527-2 | |
MD,屈服 MD, yield |
MPa | ASTM D638 | |
MD MD |
MPa | ASTM D638 | |
0.40 mm 0.40 mm 2 |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
TD,屈服 TD, yield |
% | ISO 527-2 | |
流量,屈服 Flow rate, yield |
% | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂,4 mm Fracture, 4 mm 3 |
% | ISO 527-2 | |
断裂,4 mm Fracture, 4 mm 2 |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
4 mm 4 mm |
MPa | ASTM D790 | |
4 mm 4 mm |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 4 |
|||
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ASTM D256 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 4 |
|||
-20℃ -20℃ |
ASTM D256 | ||
-20℃ -20℃ |
ISO 179 | ||
2℃ 2℃ |
ISO 179 | ||
23℃ 23℃ |
ASTM D256 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 5 |
ISO 180 | ||
Area Area |
ASTM D256 | ||
-20℃,4.00 mm -20℃,4.00 mm |
kJ/m² | ASTM D256 | |
23℃,4.00 mm 23℃,4.00 mm |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
-20℃,4 mm -20℃,4 mm |
ASTM D256 | ||
23℃,4 mm 23℃,4 mm |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 4 |
ISO 180 | ||
-20℃ -20℃ |
ISO 180 | ||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 6 | |
-- -- |
℃ | ASTM D1525 7 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Flow |
3 Across Flow |
4 4 mm thickness |
5 4 mm thick |
6 标准 B (120°C/h), 载荷2 (50N) |
7 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
山东质监局抽查风险品包装用塑料桶合格率100%
2016-09-26 危险品是易燃、易爆、有强烈腐蚀性的物品。它的运输要求非常严格,一旦发生泄漏或者其它不安全事故,将会导致不可预料的后果,严重的情况是将会对人民群众的生命财产安全造成危害。 2016年第3季度,山东省质量技术监督局组织开展了危险品包装用塑料桶、罐产品质量省监督抽查。本次共抽查了全省18家企业生产的20批次危险品包装用塑料桶、罐产品,均符合相关标准的规定。 本次抽查依据GB18191-2008《包装容器危险品包装用塑料桶》、GB19160-2008《包装容器危险品 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |