| 牌号简介 About |
|---|
| PRE-ELEC® PP 1350是一种基于聚丙烯的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。PRE-ELEC® PP 1350具有良好的机械性能平衡，易于注射成型。典型应用包括注射成型的静电放电产品，如板条箱、盒子和手提箱。 PRE-ELEC® PP 1350 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PP 1350 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded ESD products such as crates, boxes and tote bins. |
产品描述 Product Description
用途：容器;装货箱;
加工条件：注射成型 Injection Molding
性能特点： 导电; 易加工; Excellent Processability,Conductive
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.02 | g/cm³ | ASTM D792 |
|
密度 Density |
1.02 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
|
230℃，2.16kg 230℃，2.16kg |
3.5 | g/10min | ASTM D1238 |
|
230℃，5.0kg 230℃，5.0kg |
21 | g/10min | ASTM D1238 |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
230℃，2.16kg 230℃，2.16kg |
3.5 | g/10min | ISO 1133 |
|
230℃，5.0kg 230℃，5.0kg |
g/10min | ISO 1133 | |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
% | ISO 294-4 | |
|
MD MD |
% | ASTM D955 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A Shaw's A |
ASTM D2240 | ||
|
邵氏 D Shaw's D |
ASTM D2240 | ||
|
邵氏硬度 Shore hardness |
ISO 868 | ||
|
邵氏 A Shaw's A |
ISO 868 | ||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2 | |
|
4 mm 4 mm |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，4 mm Fracture, 4 mm |
% | ISO 527-2 | |
|
断裂 fracture |
% | ASTM D638 | |
|
屈服 yield |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
4 mm 4 mm |
MPa | ASTM D790 | |
|
4 mm 4 mm |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 2 |
|||
|
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ASTM D256 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 2 |
|||
|
-20℃ -20℃ |
ASTM D256 | ||
|
-20℃ -20℃ |
ISO 179 | ||
|
23℃ 23℃ |
ISO 179 | ||
|
23℃ 23℃ |
ASTM D256 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
ISO 180 | ||
|
Area Area |
ASTM D256 | ||
|
-20℃，4.00 mm -20℃，4.00 mm |
kJ/m² | ASTM D256 | |
|
23℃，4.00 mm 23℃，4.00 mm |
ASTM D256 | ||
|
-20℃ -20℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
ISO 180 | ||
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
|
-20℃，4 mm -20℃，4 mm |
ASTM D256 | ||
|
23℃，4 mm 23℃，4 mm |
ASTM D256 | ||
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 2 |
ISO 180 | ||
|
-20℃ -20℃ |
ISO 180 | ||
|
23℃ 23℃ |
ISO 180 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
|
A50 A50 |
℃ | ISO 306/A50 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ESD STM11.11 | |
|
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
|
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 4 mm thickness |
| 3 速率 A (50°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
Polymaker推出最新3D打印资料PolyMide CoPA
2018-01-18 近日，3D打印材料公司Polymaker推出了PolyMideCoPA，这是一系列基于尼龙(聚酰胺)的3D打印机线材。该线材针对“无变形”技术的工程应用进行了优化。 自从去年推出两种新型TPU基长丝以来，PolyMideCoPA是Polymaker推出的最新材料。新材料将提供黑色和自然色。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付