牌号简介 About |
---|
MAGNUM™ 3404 是一种优异的通用用途的挤出/热成型树脂,具有杰出的加工性能。该牌号综合了中等抗冲击强度和中高级的耐热性能。陶氏ABS树脂的大生产(连续工艺流程)技术可确保一种ABS树脂综合了优异的加工性能和稳定的浅基色,使其易于自着色。 应用领域: 中等抗冲击强度单层片材 共挤出片材 MAGNUM™ 3404 is an excellent general purpose extrusion / thermoforming resin with outstanding processability. It combines medium impact with medium-high heat performance. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications: Medium impact monosheet Co-extruded sheets Complies with: U.S. FDA 21 CFR 181.32(a)(3)(i) (See Notes) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ISO 1183/B |
密度 Density |
1.05 | g/cm³ | ISO 1183-2 |
熔体质量流动速率 Melt Flow Rate |
|||
220℃,10.0kg 220℃,10.0kg |
6.6 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
220℃,10 kg 220℃,10 kg |
6.70 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 to 0.70 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和 saturated |
% | ISO 62-2 | |
平衡 balance |
% | ISO 62-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 2 | |
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2 2 | |
拉伸应变 Tensile strain |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ISO 527-2/50 | |
Nominal strain at break Nominal strain at break |
% | ISO 527-2 2 | |
弯曲模量 Bending modulus 3 , 4 |
|||
3.20 mm,注塑成型 3.20 mm, injection molded 3 , 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 , 4 |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃,注塑成型 -30 ℃, injection molding |
kJ/m² | ISO 179/2C | |
-30℃,注塑成型 -30 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/2C | |
简支梁冲击强度 Charpy impact strength |
|||
23℃ 23℃ |
ISO 179/1eU 2 | ||
-30℃ -30℃ |
ISO 179/1eU 2 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃,注塑成型 -30 ℃, injection molding |
kJ/m² | ISO 180-A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-A | |
拉伸缺口冲击强度 Tensile Notch Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 8256/1 2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 2 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-2 2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 2 | |
MD MD |
1/℃ | ISO 11359-2 2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 2 | |
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
IEC 60250 2 | ||
1 MHz 1 MHz |
IEC 60250 2 | ||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
IEC 60250 2 | ||
1 MHz 1 MHz |
IEC 60250 2 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
燃烧速率 Burning rate 5 |
|||
2.0 mm 2.0 mm 5 |
mm/min | ISO 3795 | |
阻燃等级 Flame retardant level 5 |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
阻燃等级 Flame retardant level |
|||
1.60 mm 1.60 mm |
ISO 1210 2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
3 0,079 in/min |
4 3 点 |
5 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
广东要打造世界一流石化产业集群!湛江、茂名、广州、惠州、揭阳为
2020-05-22 5月20日,广东省政府网公布了《广东省人民政府关于培育发展战略性支柱产业集群和战略性新兴产业集群的意见》。 目前,广东产业已初步显现集群化发展态势。 新一代电子信息、绿 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |