牌号简介 About |
---|
LNP*COLORCOMP*310C是一种基于PBT树脂的无筋化合物。该等级的附加特征是典型的粘度为5000-7000。 LNP* COLORCOMP* 310C is an unreinforced compound based on PBT resin. Added feature of this grade is a typical viscosity of 5000-7000. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
53 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
1600 | J/m | ASTM D4812 |
落锤冲击 Drop hammer impact |
ASTM D3029 | ||
23℃ 23℃ 7 |
40.7 | J | ASTM D3029 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
154 | ℃ | ASTM D648 |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
54.4 | ℃ | ASTM D648 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM E831 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ASTM E831 | |
60 到 138℃ 60 to 138 ℃ |
cm/cm/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
1.6 mm,在空气中 1.6 mm in air |
kV/mm | ASTM D149 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance 8 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 5 |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 5 |
|||
断裂 fracture 5 |
% | ASTM D638 | |
弯曲模量 Bending modulus 6 |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 |
ASTM D790 | ||
屈服,50 mm跨度 Yield, 50 mm span |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span |
MPa | ASTM D790 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
特定体积 Specific volume |
cm³/g | ASTM D792 | |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD 3 |
% | 内部方法 | |
MD MD 4 |
% | 内部方法 | |
TD TD 3 |
% | 内部方法 | |
TD TD 4 |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt |
Pa·s | 内部方法 |
备注 |
---|
3 0.75 to 2.3 mm |
4 2.3 to 4.6 mm |
5 类型 1, 50 mm/min |
6 1.3 mm/min |
7 Modified |
8 钨电极 |
【新闻资讯】查看全部
“春风”吹来了辽阳石化的高增效
2018-06-22 6月10日,了解到,历经11天停车检修的辽阳石化聚酯线66区10万吨聚酯生产装置提前4天产出瓶级聚酯切片优级产品。据测算,仅提前生产出的产品就可以增效近百万元。转产瓶级聚酯产品,将迎来二季度高效益产品的销售“春风”。 据了解,辽阳石化聚酯线始终坚持效益导向,围绕市场需求深耕聚酯市场,着力盘活存量资源。今年3月份,聚酯生产线及相关部门通过多种渠道了解,目前瓶级聚酯切片有明显复苏迹象,并依据市场量价分析、成本效益测算等多方面因素,判断出瓶级聚酯切片市场将在二季度迎来阶段性消费旺 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |