牌号简介 About |
---|
Texin® HM-1206树脂是一种透明的高性能热塑性聚氨酯,具有标准工程热塑性塑料的硬度和模量。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.24 | g/cm³ | ASTM D792 |
密度 Density |
1.24 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:2.54 mm MD:2.54 mm |
0.50 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.17 | % | ASTM D570 |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
-30℃,3.2mm -30℃,3.2mm |
ASTM D256 | ||
23℃,3.2mm 23℃,3.2mm |
ASTM D256 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed 3 |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed 3 |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
ASTM D1525 4 | ||
A50 A50 |
ISO 306/A50 | ||
A50 A50 3 |
℃ | ISO 306/A50 | |
A50 A50 |
℃ | ISO 306/A50 | |
-- -- 3 |
℃ | ASTM D1525 4 | |
-- -- |
℃ | ASTM D1525 4 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
|||
3180 µm 3180 µm |
% | ISO 3583 | |
3180 µm 3180 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
3180 µm 3180 µm |
% | ISO 3583 | |
3180 µm 3180 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-- -- |
MPa | ASTM D790 | |
-- -- 2 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
-- -- |
MPa | ISO 178 | |
-- -- 2 |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
弯曲应变 - at Maximum Stress Bending strain - at Maximum Stress |
|||
-- -- |
% | ISO 178 | |
-- -- |
% | ASTM D790 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 | ||
洛氏硬度 Rockwell hardness |
ISO 2039-2 | ||
M 级 M-level |
ISO 2039-2 | ||
R 级 R-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 at 5% Strain |
3 Post-cured for 2 hours at 230°F |
4 速率 A (50°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
沃特新资料与东芝机械签订临时战略合作意向
2016-04-26 沃特新材料与设备供应商东芝机械株式会社在国际橡塑展第一天签署了长期战略合作意向,将在设备购买、设备研发、行业技术攻关等领域进行战略合作。 据报道,根据协议,200亩的江苏沃特新材料产业园所有挤出生产线将全部优先选用东芝机械的设备。同时,沃特将为东芝提供最前沿的新材料行业动态与需求。此外,双方将强化研发互动交流,希望能够解决一些高分子材料加工方面的行业难点,甚至取得理论上新的突破,为行业整体水平的提升做出贡献。 去年,深圳沃特集团决定建设沃特新材料项目,全套引 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |