| 牌号简介 About |
|---|
| Bayflex MP-25000是一种固体弹性体，室温下的弯曲模量为25000 psi（172 MPa）。*在反应注射成型（RIM）设备上加工，用于辊、垫圈和密封窗口。该系统结合了快速拆卸时间、良好的拆卸完整性、改进的释放特性和出色的物理性能。与任何产品一样，在给定应用中使用Bayflex MP-25000系统必须由用户提前进行测试（包括现场测试等），以确定其适用性。Bayflex MP-25000是一种配制的轮辋系统，作为两种液体成分提供。A组分为二苯基甲烷二异氰酸酯（MDI）预聚物，B组分为聚醚多元醇。注意：在将内容物从桶转移到日计量箱之前，应彻底搅动部件B。 Bayflex MP-25,000 is a solid elastomer which has a flexural modulus of 25,000 psi (172 MPa) at room temperature.* It is processed on reaction injection molding (RIM) equipment and is used for rollers, gaskets, and encapsulated windows. This system combines rapid demold times, excellent integrity at demold, improved release characteristics and outstanding physical properties. As with any product, use of the Bayflex MP-25,000 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. Bayflex MP-25,000 is a formulated RIM system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol. Note: Component B should be agitated thoroughly prior to transfer of contents from the drum to the day tank. |
产品描述 Product Description
用途：门窗;滚轴;垫圈;
加工条件：反应注射成型 (RIM)
性能特点： 含脱模剂; Good stripping performance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.04 | g/cm³ | ASTM D792 , ASTM D1622 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.0 mm MD：3.0 mm |
1.5 | % | 内部方法 |
|
吸水率 Water absorption rate |
|||
|
10days，3.00 mm 10days，3.00 mm |
5.0 | % | 内部方法 |
|
24hr，3.00 mm 24hr，3.00 mm |
3.3 | % | 内部方法 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
断裂，3 mm Fracture, 3 mm |
24.1 | MPa | ASTM D638 |
|
断裂，3 mm Fracture, 3 mm |
MPa | ASTM D412 | |
|
20% 应变 20% strain 2 |
MPa | ASTM D412 | |
|
50% 应变，3 mm 50% strain, 3 mm 3 |
MPa | ASTM D412 | |
|
100% 应变，3 mm 100% strain, 3 mm 3 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，3 mm Fracture, 3 mm |
% | ASTM D412 | |
|
撕裂强度 tear strength 4 |
|||
|
3.00 mm 3.00 mm 4 |
kN/m | ASTM D624 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Water Immersion（Length Increase，3.00 mm） Water Immersion（Length Increase，3.00 mm） |
% | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，3.00 mm Shore D, 3.00 mm |
ASTM D2240 | ||
|
弯曲模量 Bending modulus |
ASTM D790 | ||
|
-30℃，3 mm -30℃，3 mm |
MPa | ASTM D790 | |
|
23℃，3 mm 23℃，3 mm |
MPa | ASTM D790 | |
|
65℃，3 mm 65℃，3 mm |
MPa | ASTM D790 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：3 mm MD：3 mm |
1/℃ | ASTM D696 | |
|
低温脆性 Low temperature brittleness |
|||
|
-50℃，3.00 mm -50℃，3.00 mm |
ASTM D746 | ||
|
热固组件 Thermosetting components 5 |
|||
|
部件 A Component A |
|||
|
部件 B Component B |
|||
|
贮藏期限 Storage period |
|||
|
30℃ 30℃ |
wk | ||
|
脱模时间 stripping time |
min | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Die C, 20 in/min |
| 3 C 模具, 20 in/min |
| 4 C 模具 |
| 5 105 Index |
|
【新闻资讯】查看全部
全球AA市场复合年减产率估计超3%
2016-07-01 己二酸市场预计将见证3%以上的复合年均增长率。己二酸是制造尼龙的必备材料，在汽车市场有广泛的应用。 用己二酸制造的尼龙66广泛应用于汽车行业，预计会助长全球己二酸市场。己二酸同时在纺织和电子行业的应用也在增加，聚氨酯需求的增加也有望推动市场增长。制造商和消费者不断意识到对减少碳排放，这可能会增加生物己二酸的商业用途，从而加大市场需求。随着越来越多的政府福利和价格补贴，厂家已开始生产生物己二酸。 随着己二酸需求呈上升趋势，研发有望推动生物基市场。制造企业， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付