牌号简介 About |
---|
Plenco 08112是Plasglas 10112的重新编号。PLENCO 08112是一种通用聚酯散装成型化合物,其特点是在许多应用中添加了实用性。由于它具有高耐热性、良好的电气性能和强度,因此可用于铁裙板和其他小型电器外壳、线圈绕线管以及刷握等电动机部件。它可以是散装的,也可以是挤压的,目前是天然的。其他颜色可根据要求提供。它在文件E40654下被UL识别。 PLENCO 08112 is a general purpose polyester bulk molding compound that is characterized by adding utility to a number of applications. Because of its combination of high heat resistance, good electrical properties and strength. Customers have found this material useful for such applications as iron skirts and other small appliance housings, coil bobbins, and electric motor components such as brush holders. It is available in either bulk or extruded form. Colors are available upon request. It is UL recognized under file E40654. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.04 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.23 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.080 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
230 | J/m | ASTM D256 |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
240 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
连续使用温度 Continuous use temperature |
℃ | ASTM D794 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
-- -- 3 |
kV/mm | ASTM D149 | |
-- -- 4 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
E 级 E-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
3 方法B(逐步) |
【新闻资讯】查看全部
独山子石化聚丙烯新产品试产成功
2016-07-29 记者近日获悉独山子石化公司聚丙烯新产品TF1005和 TF1007试产成功。 为加快新产品的开发和产业化,优化产品结构,提高经济效益和市场竞争力,独山子石化公司将三元共聚聚丙烯产品列为新产品开发重点项目,2015年大修在新区聚丙烯装置实施丁烯-1加注系统改造,装置具备生产三元共聚聚丙烯产品的条件。 三元共聚聚丙烯具有低温热封性、透明性以及抗粘连性等特性,可满足越来越快的包装速度对薄膜热封性的更高要求,在食品、香烟、化妆品和服装等高档包装领域应用广泛。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |