牌号简介 About |
---|
LLDPE薄膜产品应用LL6910AA特别适用于贫和富混合吹塑薄膜应用,如外包装、反包装袋、收缩膜(贫混合,10-30%LLDPE)和袋装沸腾应用。该等级也推荐用于人工草地应用。LL6910AA是以己烯-1为共聚单体的线性低密度聚乙烯共聚物。它具有以下特性:非常高的刚度和向下测量潜力良好的光学特性耐高温、高水蒸气阻隔性、高蠕变、良好的密封性和收缩膜的热粘强度、较高的收缩保持力以及在需要电晕处理的情况下提高的烧穿阻力。Ry,液位通常应在38-48mn/m范围内。 LLDPE film products Applications LL6910AA is particularly suitable for use in lean and rich blend blown film applications, such as overwrap, counter bags, shrink film (lean blends, 10 to 30% LLDPE) and boil-in-the-bag applications. This grade is also recommended for artificial grass applications. Benefits and Features LL6910AA is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer. It offers the following properties: Very high stiffness and downgauging potential Good optical properties High temperature resistance High water vapour barrier properties High creep resistance Excellent sealability and hot-tack strength For shrink film, higher shrink holding force and improved burn-through resistance If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.936 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
拉伸模量 Tensile modulus |
|||
1% 正割,38 µm,吹塑薄膜 1% secant, 38 µ m, blow molded film |
450 | MPa | ISO 1184 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
18.0 | MPa | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ||
MD,38 µm,吹塑薄膜 MD, 38 µ m, blow molded film |
MPa | ||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
ISO 1184 | ||
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength 1 |
ASTM D1922 | ||
MD,38 µm MD,38 µm |
kN/m | ||
TD,38 µm TD,38 µm |
kN/m | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38 µm,吹塑薄膜 45 °, 38 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
科思创-同济-瑞好创新大赛获奖项目揭晓
2018-01-10 今日,全球领先的高科技聚合物材料生产商科思创和同济大学,携手全球聚合物解决方案专家瑞好,共同宣布“2017年科思创-瑞好先进材料设计应用大赛”暨“第二届同济-科思创创新大赛”获奖项目。来自7支优秀团队以市场为导向的创意应用设计从73个报名项目中脱颖而出,获得大奖。大赛旨在引导学生进行多学科交叉学习和创新,并提供平台助其将专业知识和技能应用到未来市场。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |