牌号简介 About |
---|
当橡胶部件需要耐油或耐溶剂性能时,建议使用尼泊尔丁腈弹性体(NBR)。尼泊尔丁腈弹性体有广泛的丙烯腈含量范围,以确保在各种条件下的最佳性能。随着丙烯腈含量的增加,燃料、油和溶剂的耐性提高;随着丁二烯含量的增加,低温柔韧性和弹性提高。为了获得广泛的硬度和其他基本性能,可以将Nipol弹性体混合以获得最佳性能。尼泊尔弹性体是最好的价值,除了最苛刻的油,热和化学应用,可在粉末,面包屑,液体和捆形式。尼泊尔丁腈弹性体特别适用于热塑性塑料和热固性改性;它们也用作涂料和粘合剂的添加剂。用于环氧树脂改性的羧基丁腈粉末,用于粘合剂和复合材料。包含滑石分区代理。nipol 1072cgx的crumb版本。 SCLAIR® 17A is a High Density Polyethylene material. It is available in North America for coextrusion. Important attributes of SCLAIR® 17A are: Butene Comonomer Food Contact Acceptable Good Processability Processing Aid Typical applications include: Additive/Masterbatch Food Contact Applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.950 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.45 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
67 | ASTM D2240 | |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
0.24 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,38 µm,吹塑薄膜 1% secant, TD, 38 µ m, blow molded film |
MPa | ASTM D882 | |
1% 正割,MD,38 µm 1% secant, MD, 38 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
MD,38 µm,吹塑薄膜 MD, 38 µ m, blow molded film |
g | ASTM D1922 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
氮传输速率 Nitrogen transfer rate |
|||
73℃,38 µm,吹塑薄膜,0.0% RH 73 ℃, 38 µ m, blow molded film, 0.0% RH |
cm³/m²/24 hr | ASTM D1434 | |
水气透过率 Water vapor transmittance |
|||
38℃,100% RH,38 µm,吹塑薄膜 38 ℃, 100% RH, 38 µ m, blow molded film |
g/m²/24 hr | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
低摩擦穿刺 Low friction puncture |
|||
吹塑薄膜,38.0 µm Blow molded film, 38.0 µ m |
J/cm | Internal Method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Measured on the base nitrile portion. |
【新闻资讯】查看全部
CHINAPLAS国际橡塑展盛装启幕 3600家展商风云际会大湾区
2021-04-13 搜料网资讯: 4月13日,CHINAPLAS 2021 国际橡塑展在深圳国际会展中心华丽启幕,上演移师深圳后的首秀。以新时代新动力永续创新为主题,展会携手全球50个国家及地区的逾3,600家展商翘楚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |