牌号简介 About |
---|
KM-4112是一种用于注塑成型的丁烯共聚物LLDPE树脂。应用包括薄壁盖子、盖子和封口以及复合材料。该产品具有优良的加工性、耐低温冲击性、优异的柔韧性和翘曲性、良好的感官性能和较高的表面光泽。KM-4112还含有加工抗氧化剂。 KM-4112 is a Butene Copolymer LLDPE resin used in injection molding. Applications include thin wall lids, caps and closures, and compounding. This grade features excellent processability, cold temperature impact resistance, outstanding flexibility and warpage resistance, good organoleptic properties and high surface gloss. KM-4112 also contains a processing antioxidant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
52 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
10.0 | hr | ASTM D1693 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -70.0 | ℃ | ASTM D746 |
维卡软化温度 Vicat Softening Temp |
87.2 | ℃ | ASTM D1525 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Snake Flow Snake Flow |
mm | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
吹塑、流延、挤出三种成膜工艺比照
2017-01-06 塑料薄膜成型方法有很多,其中流延、挤出、吹塑这三种工艺较为常见。三种工艺制膜各有特点,本文从工艺原理、应用领域两个方面进行整理分析。 工艺原理对比 流延法成膜 是通过熔体流涎骤冷生产的一种无拉伸、非定向的平挤薄膜。不存在明显的取向结构。 挤出法成膜 常见的有单向拉伸和双向拉伸法,其中双向拉伸为近几年颇为关注的生产方法。双向拉伸技术基本原理为高聚物原料先通过挤出机被加热熔融挤出成厚片,再在玻璃化温度以上熔点以下的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |