牌号简介 About |
---|
用于绝缘材料等应用中评估的柔性和非卤化阻燃挤出级。阻燃性能满足UL 1581 VW-1要求。90C或105C温度等级由UL 62 TPE类别定义。91肖氏硬度A。通常在标准挤压设备上进行的加工。使用0.12 mm x 20绞合铜导线在2.0 mm电线上进行的UL 1581试验。 Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation materials. Flame retardant performance capable of meeting UL 1581 VW-1 requirement. 90C or 105C temperature rating as defined by UL 62 TPE category. 91 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
9.0 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -40.0 | ℃ | ASTM D746 |
Heat Deformation(121℃) Heat Deformation(121℃) 7 |
5.0 | % | UL 1581 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
3.3E+16 | ohms·cm | ASTM D257 |
介电强度 Dielectric strength |
|||
2 mm,在油中 2 mm in oil |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
VW-1 VW-1 2 |
UL 1581 | ||
烟雾密度 Smoke density 8 |
|||
Flaming,Ds max:500.0 µm Flaming,Ds max:500.0 µm |
|||
Non-Flaming,Ds max:500.0 µm Non-Flaming,Ds max:500.0 µm |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,30 秒 Shore A, 30 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | UL 1581 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 4 |
MPa | UL 1581 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
% | UL 1581 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 5 |
% | UL 1581 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 6 |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
3. 类型 1, 50 mm/min |
4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
6. 13 mm/min |
7. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
8. Plaque |
【新闻资讯】查看全部
齐鲁石化乙烯装置多项关键目的持续向好
2018-01-04 2017年,齐鲁石化乙烯装置多项关键指标持续向好,其中乙烯收率完成34.32%,双烯收率完成48.35%,高附收率完成61.08%,均优于年度计划,较2016年有明显提升。 2017年,齐鲁石化烯烃厂坚持“向高指标要好效益”的工作思路,并明确了“指标再提升”的工作主题。烯烃厂从抓好原料优化入手,加大了轻质原料的投入量,尤其是LNG乙烷等原料投入量屡创新高。烯烃厂在保证裂解炉、压缩机等关键设备安全运转的基础上,通过裂解深度控制等技术手段,抓好装置的高效运行。今年检修期间,烯烃 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |